1) aluminum deoxidizing
铝脱氧
1.
The results showed that the A,B,C and D type inclusions in the trial steels,which were treated by aluminum deoxidizing and RH vacuum degassing and then were fed by core-spun yarn of rare earths in continuous casting crystallizer,were not more than 1.
结果表明,采用铝脱氧和RH真空充分脱气的微合金化碳锰钢,经连铸结晶器喂稀土处理后,钢中的A,B,C,D类夹杂物分别不大于1。
2) Si and Al deoxidation
硅、铝脱氧
3) Al-free deoxidation
无铝脱氧
4) aluminum deoxidation
加铝脱氧
5) Al final deoxidizer
铝终脱氧剂
1.
After deoxidizing in refining furnace by Al final deoxidizer and Al-Si-Ca-Ba compound deoxidizer respectively,impacting experiment at low temperature for common C grade steel casting was carried out,and the distribution and morphology of inclusions were analyzed using optical microscope and scanning electron microscope.
采用铝终脱氧剂和铝硅钙钡复合脱氧剂分别对普通C级铸钢件进行炉内脱氧精炼后进行了低温冲击性能试验,并借助光学显微镜和扫描电镜对夹杂物的分布、形貌做了分析。
6) Deoxidizer Al-Mn-Ti-Mg
铝锰钛镁脱氧剂
补充资料：铝-硅系铸造铝合金
分子式：
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。