1) hydrophilically-modified polyisocyanate
亲水改性多异氰酸酯
1.
Waterborne two-component polyurethane(2K-WPU) coatings were prepared from hydrophilically-modified polyisocyanate reacting respectively with an aqueous hydroxy-polyacrylate emulsion(PAE) and its dispersion (PAD).
分别采用水性羟基聚丙烯酸酯分散体(PAD)和羟基聚丙烯酸酯乳液(PAE)与亲水改性多异氰酸酯固化剂配制水性双组分聚氨酯涂料(2K-WPU),通过黏度、硬度、光泽度和耐化学介质性能等测试,研究了2K-WPU在不同放置时间内的物理化学行为。
2) Hydrophilic polyisocyanates
亲水多异氰酸酯
3) hydrophilic polyisocyanate crosslinking agent
亲水多异氰酸酯交联剂
4) urea-modified polyisocyanate
脲改性多异氰酸酯
5) biuret modified polyisocyanate
缩二脲改性多异氰酸酯
6) aqueous polyisocyanate curing agent
水性多异氰酸酯固化剂
1.
The effects of content of aqueous polyisocyanate curing agent in the system of two-component aqueous polyurethane adhesive for laminated films on T peel strength,ratio of absorbing water,contacting angle of glue film were studied.
研究了双组分复合薄膜用水性聚氨酯胶粘剂中水性多异氰酸酯固化剂对复合薄膜T剥离强度、胶膜的吸水率、接触角的影响。
补充资料：多苯基多亚甲基多异氰酸酯
多苯基多亚甲基多异氰酸酯，简称PAPI，或称粗MDI，浅黄色至褐色粘稠液体．有刺激性气味。相对密度(20℃／20 ℃)1．2，燃点218℃。PAPI实际上是由50％MDI与50％官能度大于2以上的多异氰酸酯组成的混合物。升温时能发生自聚作用。溶于氯苯、邻二氯苯、甲苯等。PAPI的活性低，蒸气压低，只是TDI的百分之一，故毒性很低。
用于制造聚氨脂胶粘剂。也可直接加入橡胶胶粘剂中，改善橡胶与尼龙或聚酯线的粘接性能。贮存于阴凉、通风、干燥的库房内，远离火种、热源。严格防水、防潮，避免光照。
用于制造聚氨脂胶粘剂。也可直接加入橡胶胶粘剂中，改善橡胶与尼龙或聚酯线的粘接性能。贮存于阴凉、通风、干燥的库房内，远离火种、热源。严格防水、防潮，避免光照。