1) shape memory recovery
形状记忆回复率
2) Two-way-shape-memory effect recovery ratio
双程形状记忆回复率
3) shape memory recovery ratio
形状记忆恢复率
1.
91Zralloy possesses thebest SME, shape memory recovery ratio is 74% , recoverystrain is 2.
8%时,其形状记忆恢复率为 74%,可恢复应变为 2。
4) shape memory alloys/recovery stress
形状记忆合金/回复力
5) shape recovery rate
形状回复率
1.
Experiment results showed that after quenching and up-quenching heat treatment,the shape recovery rate of the alloys increased when the solid-solution temperature changed from 650 ℃ to 900 ℃,and reached the maximum value at 850 ℃.
结果表明,在650℃至900℃范围内,经淬火加沸水时效,合金的形状回复率随着固溶温度的升高而升高,在850℃左右达到最大值,并趋于平缓。
6) shape recovery ratio
形状回复率
1.
The shape recovery ratio in Fe 14Mn 5Si 8Cr 4Ni 0.
变形后时效将合金的形状回复率提高了 190 % ,而直接时效只提高了 83 %。
2.
The shape recovery ratio in the alloy 1 with ultralow carbon contnet increases with increasing the aging time when aged at 1123K.
在 112 3K时效时 ,超低碳合金 1的形状回复率随时效时间的增加一直呈直线上升的趋势。
3.
The effects of aging time on shape memory effect,resistivity and microstructure of Fe 14Mn 5Si 8Cr 4Ni 0 2C shape memory alloy have been studied The results show that the shape recovery ratio will increase with increasing aging time,when the aging temperature is at 1123K.
结果表明 ,在 1 1 2 3K时效时 ,合金的形状回复率随时效时间的增加而升高 ,在 30 0min时达到最大值 ,比固溶态提高了 96% ;随后形状回复率随时效时间的进一步增加而缓慢下降。