1) linear porosity
条状气孔缺陷
1.
But it\'s easy to make linear porosity in welding.
在工程焊接中容易出现条状气孔缺陷。
2) sliver defect
条状缺陷
1.
The character and cause of sliver defect on IF steel sheet surface are studied by means of SEM,chemical analysis and electroanalysis.
用扫描电镜、化学和小样电解法分析了IF钢冷轧板表面条状缺陷特征及成因。
3) blowhole defect
气孔缺陷
1.
It was believed after the reason analysis that the blowhole defect was caused by the gas evolution of sand cores after being heated and the improper pouring system design which leading to the gas immixture.
介绍了493Q气缸盖的铸造工艺,分析认为气孔缺陷是因砂芯受热分解与浇注系统不合理裹入气体导致。
4) Round-hole defect
圆孔状缺陷
5) strip blistering
条状气孔
1.
Unfortunately,strip blistering defects occurred in the welds in field construction.
现场施工时,出现了条状气孔缺陷。