纳米Co3O4,Co3O4 nanoparticles,音标,读音,翻译,英文例句,英语词典

您的位置：首页 -> 词典 -> 纳米Co3O4

1) Co3O4 nanoparticles 点击朗读

纳米Co3O4

In this paper,Co3O4 nanoparticles were synthesized successfully by using low-cost,porous,reproducible bamboo charcoal as biologic template in conjunction with sol-gel method.

选用廉价、多孔、可再生的竹炭作为模板,结合溶胶-凝胶法成功地制备了纳米Co3O4。

2) Co3O4 nanoparticle 点击朗读

Co3O4纳米粉

The precursor of Co3O4 nanoparticles is synthesized through solid state reaction at ambient temperature.

随温度的升高,前驱体分解过程分两步进行:首先前驱体脱水分解为CoC2O4,然后再分解为Co3O4纳米粉。

3) Co3O4 nano-particles 点击朗读

Co3O4纳米粒子

The Co3O4 nano-particles were firstly pretreated by the silane coupling agent containing vinyl group(A-151) in order to introduce vinyl groups on their surfaces.

以含乙烯基的硅烷偶联剂(A-151)处理Co3O4纳米粒子,在Co3O4粒子表面引入乙烯基,然后以K2S2O8为引发剂,十二烷基苯磺酸钠(SDBS)为乳化剂,采用乳液聚合,在Co3O4粒子表面接枝甲基丙烯酸丁酯,研究了影响Co3O4纳米粒子表面接枝的有关因素,并优化工艺参数。

4) polystyrene/Co_3O_4() composite nanoparticles 点击朗读

聚苯乙烯/Co3O4复合纳米粒子

5) Co_3O_4 点击朗读

Co3O4

A new method is used to prepare wellseparated and spherical tricobalt tetraoxide(Co_3O_4)nanosized particles.

采用一种新方法———接枝羧基淀粉(ISC)吸附金属离子前驱物(ISC Co)热解法, 制备了粒度分布均匀、分散性好的Co3O4 纳米颗粒。

A series of Co_3O_4/Al_2O_3 catalysts were prepared via solid-state reaction and characterized by X-ray diffraction(XRD).

采用室温固相合成法制备了不同负载量的Co3O4/Al2O3系列催化剂,用X-射线衍射(XRD)技术对其物相结构进行了表征,并考察了负载量和焙烧温度对甲烷低温燃烧催化活性的影响。

A precipitation method to prepare Co_3O_4 ultrafines was reported. 点击朗读

报道了一种液相控制沉淀与分解制备Co3O4超微粉的方法。

6) Co 3O 4 点击朗读

Co3O4

Co 3O 4 nanorods have been synthesized at 160℃ for 10 h in the solution of oleic and n cetane by an emulsion solvothermal method using Co(NO 3) 2·6H 2O as starting materials.

以Co(NO3) 2 ·6H2 O为主要原料 ,H2 O2 为氧化剂 ,在油酸和正十二烷烃的混合溶液中 ,利用溶剂热技术于 160℃反应 10h ,成功地合成了Co3O4 纳米棒。

The negative electrode materials Co 3O 4 with constant particle size for lithium ion battery were prepared by mechanical milling of Co 3O 4.

采用机械球磨制备了一定粒度的锂离子电池负极材料Co3O4 。

补充资料：poly(bisphenol a-co-4-nitrophthalic anhy-dride-co

CAS：61128-46-9
分子式：(C31H20O8·C6H8N2)x
中文名称：5,5'-[(1-甲基亚乙基)双(4,1-亚苯氧基)]双-1,3-异苯并呋喃二酮与1,3-亚苯二胺的聚合物

英文名称：1,3-Isobenzofurandione, 5,5'-[(1-methylethylidene)bis(4,1-phenyleneoxy)]bis-, polymer with 1,3-benzenediamine

3-isobenzofurandione, 5,5'-[(1-methylethylidene)bis(4,1-phenyleneoxy)]bis- polymer with 1,3-benzenediamine

poly(bisphenol a-co-4-nitrophthalic anhy-dride-co

1,3-Isobenzofurandione,5,5'-[(1-methylethylidene)bis(4,1-phenyleneoxy)]bis-,polymer with 1,3-benzenediamine

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

参考词条

纳米/纳米型纳米/微米纳米(微米)

纳米-纳米纳米 Co3O4/Bi2O3 Co3O4/Fe2O3

说明：双击或选中下面任意单词，将显示该词的音标、读音、翻译等；选中中文或多个词，将显示翻译。
	您的位置：首页 -> 词典 -> 纳米Co3O4 1) Co3O4 nanoparticles 纳米Co3O4 1. In this paper,Co3O4 nanoparticles were synthesized successfully by using low-cost,porous,reproducible bamboo charcoal as biologic template in conjunction with sol-gel method. 选用廉价、多孔、可再生的竹炭作为模板,结合溶胶-凝胶法成功地制备了纳米Co3O4。 2) Co3O4 nanoparticle Co3O4纳米粉 1. The precursor of Co3O4 nanoparticles is synthesized through solid state reaction at ambient temperature. 随温度的升高,前驱体分解过程分两步进行:首先前驱体脱水分解为CoC2O4,然后再分解为Co3O4纳米粉。 3) Co3O4 nano-particles Co3O4纳米粒子 1. The Co3O4 nano-particles were firstly pretreated by the silane coupling agent containing vinyl group(A-151) in order to introduce vinyl groups on their surfaces. 以含乙烯基的硅烷偶联剂(A-151)处理Co3O4纳米粒子,在Co3O4粒子表面引入乙烯基,然后以K2S2O8为引发剂,十二烷基苯磺酸钠(SDBS)为乳化剂,采用乳液聚合,在Co3O4粒子表面接枝甲基丙烯酸丁酯,研究了影响Co3O4纳米粒子表面接枝的有关因素,并优化工艺参数。 4) polystyrene/Co_3O_4() composite nanoparticles 聚苯乙烯/Co3O4复合纳米粒子 5) Co_3O_4 Co3O4 1. A new method is used to prepare wellseparated and spherical tricobalt tetraoxide(Co_3O_4)nanosized particles. 采用一种新方法———接枝羧基淀粉(ISC)吸附金属离子前驱物(ISC Co)热解法, 制备了粒度分布均匀、分散性好的Co3O4 纳米颗粒。 2. A series of Co_3O_4/Al_2O_3 catalysts were prepared via solid-state reaction and characterized by X-ray diffraction(XRD). 采用室温固相合成法制备了不同负载量的Co3O4/Al2O3系列催化剂,用X-射线衍射(XRD)技术对其物相结构进行了表征,并考察了负载量和焙烧温度对甲烷低温燃烧催化活性的影响。 3. A precipitation method to prepare Co_3O_4 ultrafines was reported. 报道了一种液相控制沉淀与分解制备Co3O4超微粉的方法。 6) Co 3O 4 Co3O4 1. Co 3O 4 nanorods have been synthesized at 160℃ for 10 h in the solution of oleic and n cetane by an emulsion solvothermal method using Co(NO 3) 2·6H 2O as starting materials. 以Co(NO3) 2 ·6H2 O为主要原料 ,H2 O2 为氧化剂 ,在油酸和正十二烷烃的混合溶液中 ,利用溶剂热技术于 160℃反应 10h ,成功地合成了Co3O4 纳米棒。 2. The negative electrode materials Co 3O 4 with constant particle size for lithium ion battery were prepared by mechanical milling of Co 3O 4. 采用机械球磨制备了一定粒度的锂离子电池负极材料Co3O4 。补充资料：poly(bisphenol a-co-4-nitrophthalic anhy-dride-co CAS：61128-46-9 分子式：(C31H20O8·C6H8N2)x 中文名称：5,5'-[(1-甲基亚乙基)双(4,1-亚苯氧基)]双-1,3-异苯并呋喃二酮与1,3-亚苯二胺的聚合物英文名称：1,3-Isobenzofurandione, 5,5'-[(1-methylethylidene)bis(4,1-phenyleneoxy)]bis-, polymer with 1,3-benzenediamine 3-isobenzofurandione, 5,5'-[(1-methylethylidene)bis(4,1-phenyleneoxy)]bis- polymer with 1,3-benzenediamine poly(bisphenol a-co-4-nitrophthalic anhy-dride-co 1,3-Isobenzofurandione,5,5'-[(1-methylethylidene)bis(4,1-phenyleneoxy)]bis-,polymer with 1,3-benzenediamine 说明：补充资料仅用于学习参考，请勿用于其它任何用途。参考词条纳米/纳米型纳米/微米纳米(微米)

©2011 dictall.com