1) reactive hot-pressing
反应热压烧结
1.
(ZrB2-ZrO2)/BN composites were prepared by reactive hot-pressing at 1600 ℃ under 30 MPa for 90 min using BN,ZrO2,B4C and C as original materials.
采用反应热压烧结工艺制备了BN-ZrB2-ZrO2复合材料。
3) hot pressing reaction welding
热压反应烧结连接
4) activated hot pressing sintering
反应热压烧结(reactived hot pressing sintering)
5) pressureless reactive sintering
无压反应烧结
1.
With nanometer (75mol%Bi2O3+25mol%Y2O3) powder prepared by coprecipitation as raw material, the nanocrystalline Bi2O3-Y2O3 fast ionic conductor was fabricated through pressureless reactive sintering technique.
在T=600℃,t=2h无压反应烧结条件下,纳米晶Bi2O3-Y2O3 快离子导体材料的相对密度可达96％以上,并且微观结构致密均匀,很少有残留气孔和裂纹, 平均晶粒尺寸在100nm以下。
6) reaction sintering
反应烧结
1.
Microstructure and properties of Mo_2FeB_2 cermets clad layer by reaction sintering;
反应烧结三元硼化物金属陶瓷覆层的组织与性能
2.
Densification of laser ignited reaction sintering of Ni-Al-Cu powder alloy;
Ni-Al-Cu粉末合金激光点火反应烧结的致密化研究
3.
The samples prepared by general sintering and reaction sintering are investigated by XRD,SEM and other testing means for their structure and performance.
采用常规烧结法和反应烧结法烧结制品,并利用XRD和SEM等测试手段对制品的结构与性能进行了分析研究。
补充资料：反应热压烧结(reactived hot pressing sintering)
分子式：
CAS号：
性质：又称反应热压烧结(reactived hot pressing sintering)或分解热压烧结(detomposition hot pressing sintering)。利用高温下粉料可能发生某种固相物理化学反应时处于较高能量的活化状态下进行热压烧结的方法。有以下几种类型：(1)相变热压烧结，如利用氧化锆在980～1100℃之间发生相变，同时进行热压，可获得高密度的细晶陶瓷；(2)分解热压烧结，如利用镁或铝的氢氧化物(或其硫酸盐)在高温下(900～1200℃)发生脱水或释气分解时，进行热压，只需加0.3～1MPa压力，保持0.5h，就可获得高密度的制品；(3)分解合成热压烧结，利用分解反应期的高度活性，在压力作用下与异类物质产生反应，然后再在压力作用下烧结成致密陶瓷，如氢氧化钡或碳酸钡分解的氧化钡与二氧化钛合成为钛酸钡等。
CAS号：
性质：又称反应热压烧结(reactived hot pressing sintering)或分解热压烧结(detomposition hot pressing sintering)。利用高温下粉料可能发生某种固相物理化学反应时处于较高能量的活化状态下进行热压烧结的方法。有以下几种类型：(1)相变热压烧结，如利用氧化锆在980～1100℃之间发生相变，同时进行热压，可获得高密度的细晶陶瓷；(2)分解热压烧结，如利用镁或铝的氢氧化物(或其硫酸盐)在高温下(900～1200℃)发生脱水或释气分解时，进行热压，只需加0.3～1MPa压力，保持0.5h，就可获得高密度的制品；(3)分解合成热压烧结，利用分解反应期的高度活性，在压力作用下与异类物质产生反应，然后再在压力作用下烧结成致密陶瓷，如氢氧化钡或碳酸钡分解的氧化钡与二氧化钛合成为钛酸钡等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条