1) BN-ZrB2-ZrO2 composite
BN-ZrB2-ZrO2复合材料
1.
After adjusting the ratio of ZrB2 and ZrO2,the 55%BN-ZrB2-ZrO2 composite sintered at 1600 ℃,30 MPa of pressure for 90 min is possessed of more than 93% relative density.
采用反应热压烧结工艺制备了BN-ZrB2-ZrO2复合材料。
2) ZrO2-C-ZrB2 composites
ZrO2-C-ZrB2复合材料
1.
The oxidation kinetics of ZrO2-C-ZrB2 composites with 10% ZrB2 were investigated in the temperature range from 800 to 1100℃ in air by differential thermal analysis(DTA) and thermogravimetry(TG) techniques.
通过差热-热重分析研究了ZrB2含量为10%的ZrO2-C-ZrB2复合材料在800~1100℃下空气中的氧化动力学,根据气固相反应原理建立氧化动力学模型,计算反应表观活化能,并得到氧化速率与温度的经验关系式。
3) ZrB2/C composite
ZrB2/C复合材料
1.
The mass and linear ablation rates of ZrB2/C composites prepared by hot-pressing method are tested in an oxyacetylene flame with high velocity gas.
采用热压法制备ZrB2/C复合材料,利用氧乙炔火焰烧蚀法测试材料的质量烧蚀率和线烧蚀率,采用扫描电镜和X射线衍射分析材料的微观结构及物相变化。
5) CoSb_3/BN composite material
CoSb3/BN复合材料
1.
Preparation and properties of CoSb_3/BN composite material;
X射线衍射(XRD)测试表明,两者没有发生固溶或者化学反应,成功制备了CoSb3/BN复合材料。
6) ZrO_(2p)/BN-SiO_2 composite
ZrO2p/BN-SiO2复合材料
补充资料：BN
分子式 C5H10N6O2
分子量 186．18
CAS号 101-25-7
N，N-二亚硝基五次甲基四胺又称发泡剂H，简称DPT、BN，淡黄色结晶粉末，无臭。相对密度1．45～1．51。熔点207℃。溶于二甲基甲酰胺，稍梢溶于丙酮、乙醇、氯仿、甲乙酮、吡啶，不溶于冷水、乙醚。分解温度190～205℃(在空气中)、130～190 ℃(树脂中或用分解助剂)。混入硬脂酸或尿素时，可使分解温度降低。发气量260～270mL／g。分解产物主要是氮气，有少量一氧化碳、二氧化碳、甲醛
等气体。加入尿素可梢除分解产物臭味。易燃．与酸或酸雾接触会迅速起火燃烧，当摩擦和敲击时可能自燃。对皮肤和粘膜有中等刺激性。
用作胶粘剂或密封剂的发泡剂。贮存于阴凉、通风、干燥的库房内，远离火种、热源。
分子量 186．18
CAS号 101-25-7
N，N-二亚硝基五次甲基四胺又称发泡剂H，简称DPT、BN，淡黄色结晶粉末，无臭。相对密度1．45～1．51。熔点207℃。溶于二甲基甲酰胺，稍梢溶于丙酮、乙醇、氯仿、甲乙酮、吡啶，不溶于冷水、乙醚。分解温度190～205℃(在空气中)、130～190 ℃(树脂中或用分解助剂)。混入硬脂酸或尿素时，可使分解温度降低。发气量260～270mL／g。分解产物主要是氮气，有少量一氧化碳、二氧化碳、甲醛
等气体。加入尿素可梢除分解产物臭味。易燃．与酸或酸雾接触会迅速起火燃烧，当摩擦和敲击时可能自燃。对皮肤和粘膜有中等刺激性。
用作胶粘剂或密封剂的发泡剂。贮存于阴凉、通风、干燥的库房内，远离火种、热源。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条