1) phase glaze
分相花釉
1.
And then, the formation mechanism of phase glaze was explored.
针对还原焰烧成陶瓷西餐具的需要,对还原焰分相花釉的釉料组成、工艺条件、外观效果、低倍结构作了实验研究,并进一步探讨了分相花釉的形成机理。
2) phase separation art glaze
分相艺术釉
1.
Discussed the mechanism of phase separation kiln change, and then analysed the reasons of pinhole and glaze bubble in phase separation art glaze.
论述了分相窑变釉形成的基本原理,分析了分相艺术釉针孔和釉泡形成的原因,得出了除烧成温度太高或太低、素烧坯不到位、坯体挥发所致之外,还有一种新的可能,那就是SiC的落渣所致的结论。
3) Phase-Separated Opalescent Glaze
分相乳光釉
4) fancy glaze
花釉
1.
This paper mainly describes the preparation and application of high quality mat and gelatine-pad printed fancy glaze,analyzes the frit composition of gelatine-pad printed fancy glaze,its raw materials,glaze preparing process and other influences on the effect of gelatine-pad printing art.
本文首先叙述了高档无光凸印花釉的试制过程 ,然后较详细地分析了凸印花釉熔块的构成、生料的组成、凸花釉的制作工艺和其它因素对凸花艺术效果的影响。
5) colour produced in glaze by "unstable" decomposion
釉的分相呈色
6) Infiltrated Glaze
渗花釉
1.
With orthogonalizing design meth od,the influence that Ni 2+ ?Cu 2+ ?Co 2+ ?Fe 3+ ?Cr 6+ transition metal ions were used for the black infiltrated glaze on the vitrr ous tile were explored.
本文运用正交法法,探讨了过渡金属Ni2+、Cu2+、Co2+、Fe3+、Cr6+离子用于呈黑色渗花釉的影响。
补充资料：分相
分相
phase separation
fenxiang分相(phase separation)硅酸盐熔体和玻璃中某些组分在一些区域内偏聚形成化学组成不同相的现象.20世纪90年代以来用电镜对二、三组分和多组分玻瑞进行的研究表明，所有玻璃都有微不均区(分相)，例如AI:03一510:系在A120:含量10%~50%范围，在小于1600℃存在着分相区域，这对耐火纤维使用中的变化有重要意义。分相的根本原因是热力学自由烤的降低，其机理有成核生长与不稳分解两种，前者组成变化大，但是空间分布范围小;后者组成变化小而空间弥散范围大。分相造成亚微结构不均匀。 (李晓明)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。