2) polymeric pentaerythrityl phosphate
聚季戊四醇磷酸酯
1.
)first in the absence of organic solvent,and then an oligomer polymeric pentaerythrityl phosphate was synthesized in yield 79% from PDD and hydroquinone(1equiv.
以季戊四醇、三氯氧磷为原料,采用无溶剂法首先合成了季戊四醇二磷酸酯二磷酰氯(PDD),n(季戊四醇)n∶(三氯氧磷)=1 5∶,收率为84%;然后以PDD和对苯二酚为原料,乙腈为溶剂,三乙胺为缚酸剂,在氮气氛围下合成了低聚阻燃剂聚季戊四醇磷酸酯,n(PDD)∶n(对苯二酚)=1∶1,收率为79%。
2.
) first in the absence of organic solvent, and then an oligomer polymeric pentaerythrityl phosphate was synthesized in yield 79% from PDD and hydroquinone (lequiv.
以季戊四醇、三氯氧磷为原料,采用无溶剂法首先合成了季戊四醇二磷酸酯二磷酰氯(PDD),n(季戊四醇):n(三氯氧磷)=1:5,收率为84％;然后以PDD和对苯二酚为原料,乙腈为溶剂,三乙胺为缚酸剂,在氮气氛围下合成了低聚阻燃剂聚季戊四醇磷酸酯,n(PDD):n(对苯二酚)=1:1,收率为79％。
3) Pentaerythritol Biphosphate
季戊四醇型双磷酸酯
1.
Study on Synthesis and Application of Pentaerythritol Biphosphate Fire Retardant;
季戊四醇型双磷酸酯阻燃剂的合成及应用研究
4) pentaerythritol phosphate
季戊四醇型磷酸酯
5) melamine salt of pentaerythritol phosphate
季戊四醇磷酸酯蜜胺盐
1.
And in order to reduce the emission of pollutant,the intumescent flame retardant named melamine salt of pentaerythritol phosphate(MPP) was synthesized from phosphoric acid instead of phosphorus oxychloride(POCl_3) in the conventional technology.
(1)利用溶剂法制备了三聚氰胺磷酸盐(MP)、三聚氰胺焦磷酸盐(MPY)和三聚氰胺聚磷酸盐(MPOP),并用磷酸为原料代替传统的三氯氧磷制备了季戊四醇磷酸酯蜜胺盐(MPP),减少了污染物的排放,并通过对中间体-季戊四醇磷酸酯的制备及表征,推测出季戊四醇磷酸酯蜜胺盐(MPP)的结构及反应机理;(2)利用新颖的固相化学法制备了三聚氰胺聚磷酸盐(MPOP)和季戊四醇磷酸酯蜜胺盐(MPP),制备过程环保无污染;(3)本文考察了反应温度、反应时间及其原料比等条件对反应的影响,并通过单因素及正交实验得出溶剂法和固相化学法的较佳合成工艺;利用FT-IR、MS、NMR、TG、DSC等方法对产物的结构、热性能进行表征与测试,结果表明产物红外光谱图与文献基本一致,同时初步探究了其反应机理和阻燃机理。
6) PEPA
笼状季戊四醇磷酸酯
1.
The intumescent flame retardant(IFR) PP was prepared by using Melamine polyphosphate(MPP) and 1-oxo-4-hydroxymethy1-2,6,7-trioxa-1-phosphabicyclooctane(PEPA) as flame retardants and Cr2O3 as synergistic agent.
以Cr2O3为阻燃协效剂,采用多聚磷酸蜜胺(MPP)和笼状季戊四醇磷酸酯(PEPA)复配阻燃剂,制备了具有良好阻燃性能的无卤阻燃PP。
2.
Halogen-free flame retardant polypropylene(PP) was prepared by using melamine polyphosphate(MPP) and 1-oxo-4-hydroxymethy 1-2,6,7-trioxa-1-phospha-bicyclooctane(PEPA) as flame retardants.
采用多聚磷酸蜜胺(MPP)和笼状季戊四醇磷酸酯(PEPA)复配阻燃剂,制备了具有良好阻燃性能的无卤阻燃PP。
3.
Intumescent flame retardant(IFR) polypropylene(PP) was prepared by using Melamine polyphosphate(MPP) and 1-oxo-4-hydroxymethy1-2,6,7-trioxa-1-phospha-bicyclo-octane(PEPA) as flame retardants and 4A Zeolite as synergistic agent.
以4A分子筛为阻燃协效剂,采用多聚磷酸蜜胺(MPP)和笼状季戊四醇磷酸酯(PEPA)复配阻燃剂,制备了具有良好阻燃性能的无卤阻燃PP。
补充资料：季戊四醇
| 季戊四醇 pentaerythritol 一种多元醇，分子式 C（CH2OH ）4。又称四羟甲基甲烷或二羟甲基-1，3-丙二醇。  白色或淡黄色结晶粉末。熔点 269℃。易溶于热水，在冷水中溶解度较小，微溶于乙醇。季戊四醇与氢溴酸或氢碘酸反应，生成二卤代醇，然后再生成四卤代烃，后者与乙醇钠反应，则生成季戊四醇四乙基醚；与硝酸反应生成四硝酸季戊四醇酯，此化合物为无色晶体，熔点140～141℃，对碰撞极敏感，是强爆炸力炸药，也是长效抗心绞痛药；与氯化亚砜反应，生成亚硫酸季戊四醇酯；在盐酸或氯化锌存在下与醛或酮反应生成缩醛或缩酮，当醛量不足时只生成单缩醛。季戊四醇是用甲醛和乙醛在碱水溶液中缩合、还原制备。反应时先生成三羟甲基乙醛，然后再经甲醛还原即得产物 。以上反应有较多副反应，应严格控制原料配比和反应温度 。季戊四醇是制作油漆、涂料、合成树脂和炸药的重要原料 。 |