1) methoxy poly(ethylene glycol)-poly(isooctyl-cyanoacrylate)
聚乙二醇单甲醚-聚氰基丙烯酸异辛酯
3) methylacrylic acid polyethylene glycol single methyl ether-750 ester(MAAPEGME-750)
甲基丙烯酸聚乙二醇单甲醚-750酯(MAAPEGME-750)
4) methylacrylic acid polyethylene glycol single methyl ether(400) ester
甲基丙烯酸聚乙二醇单甲醚(400)酯
5) MPEG-MAA
甲基丙烯酸聚乙二醇单甲醚酯
1.
The synthesization technics of MPEG-MAA was studied in this paper,which is an important intermediate used for preparation of polycarboxylate superplasticizer.
本文对制备聚羧酸系减水剂的重要中间体——甲基丙烯酸聚乙二醇单甲醚酯的合成工艺进行了研究,考察了反应时间、催化剂对甲苯磺酸的用量、阻聚剂对苯二酚的用量、反应温度及甲基丙烯酸(MAA)与聚乙二醇单甲醚(MPEG)的用量比对酯化率的影响。
6) methoxy polyethylene glycol methacrylate(MPEGMA)
聚乙二醇单甲醚甲基丙烯酸酯
1.
The macromer,methoxy polyethylene glycol methacrylate(MPEGMA),used for polycarboxylate based superplasticizer was prepared by esterification of methacrylic acid(MAA) and methoxy polyethylene glycol(MPEG).
以聚乙二醇单甲醚(MPEG)和甲基丙烯酸(MAA)为主要原料,通过酯化反应制备聚羧酸系减水剂大单体聚乙二醇单甲醚甲基丙烯酸酯(MPEGMA)。
补充资料:聚乙二醇
聚乙二醇又称聚乙二醇醚,简称PEG,结构式为HO(CH2CH2O)nH,根据分子量大小不同,可从无色透明粘稠液体(分子量200~700)到白色脂状半固体(分子量1000~2000)直至坚硬的蜡状固体(分子量3000~20000),相对密度(20℃/20 ℃)1.12~1.15。作为增韧利用的聚乙二醇主要是分子量200~600的室温下为无色透明的粘性液体,无味。易溶于水,溶于甲醇、乙醇、丙酮、醋酸乙酯、苯、甲苯、二氯乙烷、三氯乙烯等.不溶于脂肪烃。对酚类溶解能力强,当皮肤上附有苯酚、甲酚时,可用分子量约400的聚乙二醇除去。与硝酸纤维素、松香、酪阮可以混合.但对一般的合成树脂不溶解,对橡胶也不溶胀。吸湿性大。聚乙二醇在正常条件下是很稳定的,但在120 ℃或更高温度下能与空气中的氧发生氧化作用。加热至300 C产生断裂或热裂解。聚乙二醇不挥发.闪点高,对金屑无腐蚀性。无毒,对眼睛和皮肤无明显刺激,LD5033000~43000mg/kg。
用作环氧树脂和聚乙烯醇的增韧剂。
贮存于干燥的库房内,远离火源。
用作环氧树脂和聚乙烯醇的增韧剂。
贮存于干燥的库房内,远离火源。