1) directional PMMA
定向有机玻璃
1.
In order to improve poor adhesion strength between Polyurethane interlayer(PU) and directional PMMA plate interface,IPN compounds,which are consistent in thermodynamics with both substrates,are prepared to increase interfacial adhesion strength.
在异质的透明材料复合过程中,针对聚氨酯胶片(PU)与定向有机玻璃(D-PMMA)界面粘结强度低的问题,本论文拟以一定溶剂溶解聚氨酯胶片,并在其溶液中引发丙烯酸同系物的聚合反应,形成一种类似互穿网络的热力学相容体系,以该体系改善界面的粘接强度。
2.
In order to improve adhesion strength between Polyurethane interlayer(PU) and directional PMMA plate,IPN compounds,which are consistent in thermodynamics with both substrates,are prepared to increase interfacial adhesion strength.
在异质的透明材料复合过程中,针对聚氨酯胶片(PU)与定向有机玻璃(D-PMMA)界面粘结强度低的问题,该论文拟以一定溶剂溶解聚氨酯胶片,并在其溶液中引发丙烯酸同系物的聚合反应,形成一种类似互穿网络的热力学相容体系,以该体系改善界面的粘接强度。
2) orientation of organic glass
有机玻璃定向
3) Polymethyl methacrylate
有机玻璃
1.
Tension and bending fatigue tests were carried out to investigate the fatigue behavior of polymethyl methacrylate for edge attachment element at different temperatures.
研究了有机玻璃边缘连接元件在不同温度下的拉伸和弯曲疲劳特性。
2.
For polymethyl methacrylate(PMMA),pure mode I fracture tests were performed under quasi-static loading by using central notched circular disk specimen.
采用直槽式和尖槽式中心切口圆盘试件,对有机玻璃在纯Ⅰ型准静态加载条件下的断裂行为进行了实验研究。
3.
Mechanical and optical functions of polymethyl methacrylate were analyzed in this paper.
首次对国产有机玻璃的力学性能、光学性能等性质进行了全面研究 ,通过试验得到了常温和冻结温度的有机玻璃的性能数据 ,提出了常温时光塑性条纹是应变条纹 ,冻结温度下光塑性条纹是应力条纹的新观点。
4) Organic Glass
有机玻璃
1.
Study on Preparation and Performance of Organic Glass Containing Pb by Microemulsion Polymerization;
利用微乳液制备含铅有机玻璃及其性能研究
2.
Effect of Molecular Structure of Organic Glass on Property;
有机玻璃的分子结构对其性能的影响
3.
Investigation on Production of Organic Glass Craftworks by Casting Bulk Polymerization;
铸塑本体聚合法生产有机玻璃工艺制品研究
5) plexiglass
[英]['pleksiglɑ:s] [美]['plɛksɪ,glæs]
有机玻璃
1.
Development of the aviation plexiglass drawing force digital PID control system;
航空有机玻璃拉伸机拉伸力数字PID控制系统开发
2.
Results indicate that plexiglass protective layers have better adhesion than silicate protective layers;with the increasing of temperature and holding time,adhesion of silicate protective layers is going up at first and then down,while that of plexiglass rises at first and then don't change;cooling mode has great influence on adhesion of silicate protective layers,while it has no impact on.
结果表明:有机玻璃防护层的结合强度较硅酸盐玻璃的高;随着制备温度和保温时间的增加,硅酸盐玻璃防护层的结合强度先上升后下降,而有机玻璃防护层的结合强度上升后不再变化。
3.
The result of the experiment shows that if add crosslinking TAIC and plasticizer phthalate to the ploymer,heat resistance and brittleness of plexiglass could be modified.
2%)和增塑剂邻苯二甲酸二丁酯(用量为单体用量的8%～12%),可改进有机玻璃的耐热性和脆性。
6) PMMA
有机玻璃
1.
Study on Novel Technique for Preparation of PMMA;
一种制备纯有机玻璃的新工艺研究
2.
Experimental Research on The Constitutive Relationship of PMMA;
有机玻璃本构关系的试验研究
3.
Study of Improvement of Antistatic Property of PMMA by Plasma Surface treatment;
等离子体表面改性法改善有机玻璃抗静电性能的研究
补充资料：彩色有机玻璃
分子式：
CAS号：
性质：有色有机玻璃的通称。性能和普通有机玻璃相同。将染料或颜料预先溶解或均匀分散于甲基丙烯酸甲酯单体(或预聚浆料)中，经本体聚合制得。分透明、半透明和不透呀三种。染料溶于单体的是透明彩色有机玻璃。颜料分散于单体的是不透明彩色有机玻璃。色料和聚苯乙烯或液体石蜡同时溶于单体的是半透明彩色有机玻璃。主要用于广告标牌，装潢装饰、日用器具等领域。
CAS号：
性质：有色有机玻璃的通称。性能和普通有机玻璃相同。将染料或颜料预先溶解或均匀分散于甲基丙烯酸甲酯单体(或预聚浆料)中，经本体聚合制得。分透明、半透明和不透呀三种。染料溶于单体的是透明彩色有机玻璃。颜料分散于单体的是不透明彩色有机玻璃。色料和聚苯乙烯或液体石蜡同时溶于单体的是半透明彩色有机玻璃。主要用于广告标牌，装潢装饰、日用器具等领域。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条