1) cementitious minerals
胶凝性矿物
1.
The results showed that the contents of major cementitious minerals such as C3S,C2S,C6AF2 and C6A2F increase.
结果表明:经高温重构后,钢渣中C3S、C2S、C6AF2、C6A2F等胶凝性矿物含量有不同程度的增加,水化反应的放热速率和放热量都远高于未重构的钢渣;当钢渣﹕矿渣﹕工业石灰的质量比为60﹕15﹕25和重构温度为1350℃时,重构后钢渣的活性指数可达到0。
2) mineral gel
矿物凝胶
1.
When processed into mineral gel through purification, modification and composition processes, it has found wider applications and become far more valuable in industry.
经过提纯、改型、改性、复合等工序,将它加工成矿物凝胶,便有了更广泛的用途,其价值也提高了几十倍乃至上百倍。
3) mineral inorganic gel
矿物无机凝胶
1.
Bentonite is selected to be treated by purification,retrofit,modification and gelatination to form mineral inorganic gel.
膨润土经分选提纯、钠化改型、磷化改性及胶化等主要工序可制备得到具有广泛应用前景的矿物无机凝胶。
4) alaterite
矿物性生橡胶
5) high performance slag materials
高性能矿渣胶凝材料
补充资料：胶凝
胶凝
supermolecule,micelle
』iaoshu胶束(。upermoleeule，。ieelle)表面活性剂在溶液中的浓度超过一临界值后，活性剂的离子或分子缔合形成的缔合胶体.胶束的成因是:当溶液中表面活性剂浓度增加时，具有僧水和亲水攀团的活性分子就会被吸附到气一液界面上，形成定向排列，结基使表面张力降低.但当活性荆浓度增加到一定值时表面就会被一层活性剂分子(或离子)占满.再增大浓度时，表面已不娜拜容纳更多的分子(或禽子)·表面张力也不会再降低，此时就会出现成团的结构。这种成团结构就是绮合胶体—胶束。它是由活性剂分子的僧水基团互相缔合形成的，亲水基团则留在缔合体的表面，与水相接触，这样可使界面能降到最低.开始形成胶束的浓度称为临界胶束浓度，用CMC表示。胶束的形状有球状、棒状、层状等。(见图)离子型表面活性荆胶束 单象翼束O馨①豹溥 棒状胶束层状胶束 各种胶柬形态是由离子缔合而成的，它是带电的，也称胶体电解质。非离子型表面活性剂胶束也是由表面活性剂分子缔合而成的，但不属于胶体电解质.表面活性剂在溶液中开始形成胶束的“临界胶束浓度”前后，溶液的一些物理性质，如渗透压、浊度、表面张力、电导率等都会发生显著变化。因此在使用表面活性剂中必须注意，否则会造成相反的效果.如在耐火浇注料中加人作为减水与分散作用的表面活性剂时，浓度超过“临界胶束浓度CMC”时，反而会使浇注料的流动性变差。 (李再拼)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条