1) Carbon distribution in the carburized layer
渗层碳分布
2) carbon concentration distribution
渗层碳浓度分布
1.
Carburized case depth and carbon concentration distribution model was established in this paper.
建立了不同渗碳条件下渗碳层深度和渗层碳浓度分布模型,通过VisualBasic程序设计语言开发了常用渗碳材料渗层碳浓度分布的数值模拟系统。
4) cementite distribution
渗碳体分布
1.
In order to find out reasons of different deep drawing properties of two kinds of cold rolled sheets that produced with traditional process and short production process,a series of tests,such as chemical compositions,microstructures,cementite distribution and inclusion types are made.
通过对传统流程和短流程冷轧深冲板化学成分、微观组织、渗碳体分布以及夹杂物类型的检测,研究2种冷轧深冲板性能差异的原因。
5) carburizing atmosphere distribution
渗碳气氛分布
6) carburized layer
渗碳层
1.
The results show the things as follows:Firstly,in the surface,it was decarbonized,and the depth of carburized layer is not deep enough; Secondly,in the carburized layer,the grain size of metallography organization is too large;Thirdly,there was edge load running during service.
对失效件进行宏观分析、断口微观分析、齿面显微分析等,结果表明:齿表面渗碳层深度不足,并有脱碳现象,渗碳层组织粗大,使用中存在偏载现象等问题,是造成齿轮轴伞齿段发生崩齿失效的主要原因。
2.
The surface microhardness of sample A is higher than that of sample B and the carburized layer of sample A is thi.
表面显微硬度比较发现,试样A的硬度明显高于试样B,在光学显微镜下观察两试样的截面,试样A渗碳层的厚度明显大于试样B。
3.
It is discovered that there is carburized layer, small chamfer and coarseness surface.
通过扫描电镜观察、金相检验、化学分析以及硬度检测等手段,对中厚板轧机传动部位的十字接轴断裂的原因进行了分析,发现轴根部存在渗碳层并且变截面处圆角较小、表面加工较粗糙。