2) reactive hot-pressing
反应热压烧结
1.
(ZrB2-ZrO2)/BN composites were prepared by reactive hot-pressing at 1600 ℃ under 30 MPa for 90 min using BN,ZrO2,B4C and C as original materials.
采用反应热压烧结工艺制备了BN-ZrB2-ZrO2复合材料。
3) hot pressing reaction welding
热压反应烧结连接
4) activated hot pressing sintering
反应热压烧结(reactived hot pressing sintering)
5) pressureless reactive sintering
无压反应烧结
1.
With nanometer (75mol%Bi2O3+25mol%Y2O3) powder prepared by coprecipitation as raw material, the nanocrystalline Bi2O3-Y2O3 fast ionic conductor was fabricated through pressureless reactive sintering technique.
在T=600℃,t=2h无压反应烧结条件下,纳米晶Bi2O3-Y2O3 快离子导体材料的相对密度可达96％以上,并且微观结构致密均匀,很少有残留气孔和裂纹, 平均晶粒尺寸在100nm以下。
6) reaction sintering
反应烧结
1.
Microstructure and properties of Mo_2FeB_2 cermets clad layer by reaction sintering;
反应烧结三元硼化物金属陶瓷覆层的组织与性能
2.
Densification of laser ignited reaction sintering of Ni-Al-Cu powder alloy;
Ni-Al-Cu粉末合金激光点火反应烧结的致密化研究
3.
The samples prepared by general sintering and reaction sintering are investigated by XRD,SEM and other testing means for their structure and performance.
采用常规烧结法和反应烧结法烧结制品,并利用XRD和SEM等测试手段对制品的结构与性能进行了分析研究。
补充资料：热压
热压
hot pressing
reyo热压(hot pressing)一种将模压与烧结相结合的成形方法，又称静热压(statie hot pressing)、加压烧结，也称活化烧结。它是将金属粉末装在模腔内，平稳地加压同时将粉末加热到正常的烧结温度或稍低一些的温度，经过较短的时间，烧结成致密而均匀的制品。为了使预热粉末或预压压坯不被空气氧化或氮化，热压过程必须在保护气氛或真空下进行。热压模的选择原则一般是:低温高压工艺可选择金属或硬质合金模;高温高压工艺则选择石墨模。尽管人们对加压烧结和热压这两个术语交叉使用，但这两个工艺过程却各有侧重。在加压烧结中，强调的是热过程;在热压中则着重强调施加的压力是主要的可调变量。热压技术的特点是:粉末致密化以及脱模所用的设备和工序与冷压和烧结工艺无区别，所不同的是热压时间较长，即在特定的压力及温度下，通过塑性变形、蠕变及扩散使粉末压坯充分密实所需的时间较长，因此生产率降低，成本较高。但由于热压工艺可大大降低成形压力(为冷压成形的十分之一)，缩短烧结时间，制造密度极高、晶粒极细的材料，它们常用来制造硬质合金及陶瓷刀具、拉丝模及大型、异形薄壁管、薄片，还可以压制硬而脆的碳化硼及陶瓷制品。 在密闭模中热压金属粉末是粉末冶金方法中最古老的方法之一。1912年和1917年德国和美国分别获得了钨和碳化钨粉热压制造致密件的专利，1920年以后欧洲和美国生产了圆柱形的拉丝模，从1930年起热压技术发展更快。近年来又发展了真空热压和振动热压，为了提高生产率还研制出实现连续热压的竖式和卧式连续热压机。 (张齐勋)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。