1) technology harmonization of pickling and acid regeneration line
酸洗-酸再生工艺协调
3) pickling technology
酸洗工艺
1.
According to pickling technology,this article provides effective methods for the acid concentration test and strip quality control in Turboflow pickling.
本文就酸洗工艺,对紊流酸洗酸液浓度检测及带钢酸洗质量的控制等提供了行之有效的方法。
2.
The disadvantages of current technology of metal strip pickling were discussed,After some improvement of the pickling technology for metal strips,the speed and adjustment ability of the pickling line and the quality of pickling were improved.
对现有金属带酸洗工艺的不足之处,进行了适当改进,提高了连续酸洗工艺生产线的调节能力、酸洗速度和酸洗质量。
4) pickling process
酸洗工艺
1.
A Test for Pickling Process of S31803 Austenite-Ferrite Duplex Phase Stainless Steel;
S31803双相不锈钢酸洗工艺的试验
5) copper part
铜酸洗工艺
6) buck souring
温酸洗工艺
补充资料：酸洗
分子式：
CAS号：
性质：(一)利用酸溶液去除钢铁表面上的氧化皮和锈蚀物的方法称为酸洗。氧化皮、铁锈等铁的氧化物(Fe3O4，Fe2O3，FeO等)与酸溶液发生化学反应，形成盐类溶于酸溶液中而被除去。酸洗用酸有硫酸、盐酸、磷酸、硝酸、铬酸、氢氟酸和混合酸等。最常用的是硫酸和盐酸。酸洗工艺主要有浸渍酸洗法、喷射酸洗法和酸膏除锈法。一般多用浸渍酸洗法，大批量生产中可采用喷射法。钢铁零件一般在10％～20％(体积)硫酸溶液中酸洗，温度为40℃。当溶液中含铁量超过80g/L，硫酸亚铁超过215g/L时，应更换酸洗液。常温下，用20％～80％(体积)的盐酸溶液对钢铁进行酸洗，不易发生过腐蚀和氢脆现象。由于酸对金属的腐蚀作用很大，需要添加缓蚀剂。(二)为了消除硅藻土载体表面吸附，减少色谱峰拖尾，载体在使用前需进行酸洗或碱洗处理。酸洗是把载体用6mol/L盐酸浸煮2h或浓盐酸加热浸煮30min，过滤，用水洗至中性，烘干。酸洗可除去表面上的铁、铝、钙、镁等杂质，但不能除去硅醇基。酸洗载体适宜于分析酸性样品。
CAS号：
性质：(一)利用酸溶液去除钢铁表面上的氧化皮和锈蚀物的方法称为酸洗。氧化皮、铁锈等铁的氧化物(Fe3O4，Fe2O3，FeO等)与酸溶液发生化学反应，形成盐类溶于酸溶液中而被除去。酸洗用酸有硫酸、盐酸、磷酸、硝酸、铬酸、氢氟酸和混合酸等。最常用的是硫酸和盐酸。酸洗工艺主要有浸渍酸洗法、喷射酸洗法和酸膏除锈法。一般多用浸渍酸洗法，大批量生产中可采用喷射法。钢铁零件一般在10％～20％(体积)硫酸溶液中酸洗，温度为40℃。当溶液中含铁量超过80g/L，硫酸亚铁超过215g/L时，应更换酸洗液。常温下，用20％～80％(体积)的盐酸溶液对钢铁进行酸洗，不易发生过腐蚀和氢脆现象。由于酸对金属的腐蚀作用很大，需要添加缓蚀剂。(二)为了消除硅藻土载体表面吸附，减少色谱峰拖尾，载体在使用前需进行酸洗或碱洗处理。酸洗是把载体用6mol/L盐酸浸煮2h或浓盐酸加热浸煮30min，过滤，用水洗至中性，烘干。酸洗可除去表面上的铁、铝、钙、镁等杂质，但不能除去硅醇基。酸洗载体适宜于分析酸性样品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。