Polysilicate-metals flocculants of various molar ratio of Al to Si,Fe to Si and(Al+Fe) to Si are prepared,such as polysilicate aluminum chloride(PASC),polysilicate ferric sulfate(PFSS),ploysilicate-aluminum-ferric(PFASC).
制备了不同Al∶Si、Fe∶Si和(Al+Fe)∶Si摩尔比的聚硅酸金属盐系列絮凝剂:聚硅氯化铝(PASC)、聚硅硫酸铁(PFSS)和聚硅硫酸铁氯化铝(PFASC),实验考察了成分摩尔比、废水pH值、絮凝剂投加量对除油效果的影响。
3) polysilicate aluminum ferrite chloride
聚硅酸氯化铁铝
1.
Take the sodium silicate,the ferric chloride and the aluminum chloride prepared the high stability as the raw material research to polysilicate aluminum ferrite chloride(PAFSC).
以水玻璃,氯化铁和氯化铝为原料研究制备了高稳定性聚硅酸氯化铁铝(PAFSC)。
4) PSAFC
聚硅酸氯化铝铁
1.
Appropriate amount of activated metasilicic acid is added to the leach solution to produce PSAFC.
红黄土壤经焙烧活化后 ,用工业废盐酸浸渍 ,向浸出液中加入适量活性硅酸 ,制备成聚硅酸氯化铝铁。
5) polyaluminium ferric sulfatochloride
聚硫酸氯化铝铁
1.
In this paper, main research focuses on the influence of the amount of polyaluminium ferric sulfatochloride(PAFCS),polyaluminium chloride(PAC) and polyferric sulphate(PFS) on flocculating results and the range of pH value in which PAFCS may produce the best tubidity removal effect.
文章研究了聚硫酸氯化铝铁 ( PA FCS)、聚合氯化铝 ( PA C)和聚合硫酸铁 ( PFS)投加量对絮凝效果的影响以及PAF CS使用 p H范围 ,比较了 PAFCS、氯化铁 ( FC)和硫酸铝 ( A S)的脱色效果 ,探讨了水中残留铝的脱除。
6) PSFCS
聚硅氯化硫酸铁
1.
The processing conditions of using hydrochloric acid,sulphuric acid,limonite and sodium silicate as raw materials to prepare poly-silicic-ferric chloride sulfate(PSFCS) flocculant are discussed by means of the perpendicular experiment.
通过正交实验研究了用盐酸、硫酸、褐铁矿和硅酸钠制备聚硅氯化硫酸铁(PSFCS)絮凝剂的工艺条件。
2.
The processing conditions of using hydrochloric acid,sulphuric acid,pyrite cinder and sodium silicate as raw materials to prepare poly-silicic-ferric chloride sulfate(PSFCS) flocculant were tested by means of orthogonal experiment method.
通过正交实验研究了用盐酸、硫酸、硫铁矿烧渣和硅酸钠制备聚硅氯化硫酸铁(PSFCS)絮凝剂的工艺条件。
3.
Low-grade hematite,hydrochloric acid,sulphuric acid and sodium silicate were used to prepare poly-silicic-ferric chloride sulfate(PSFCS).
以低品位赤铁矿、盐酸、硫酸和硅酸钠为原料,制备了聚硅氯化硫酸铁(PSFCS)混凝剂,对合成过程及工艺条件进行了研究。
补充资料：聚[3,3-双(氟甲基)氧杂环丁烷]
分子式：
CAS号：
性质： 以氟原子取代氯的卤化聚醚树脂类似物。同氯化聚醚一样，经拉伸和极化处理的该类树脂也表现出压电和热电性质。由于分子中碳氟键的极性比碳氯键大，预期在热电性质方面具有优越性质，而且氟取代物的碳氟键能高，其化学稳定性要好于氯取代类似物。聚[3,3-双(氟甲基)氧杂环丁烷]的合成与聚[3,3-双(氯甲基)氧杂环丁烷]的制备类似，首先合成3,3-双(氟甲基)氧杂环丁烷，然后利用开环聚合反应得到该聚合物。
CAS号：
性质： 以氟原子取代氯的卤化聚醚树脂类似物。同氯化聚醚一样，经拉伸和极化处理的该类树脂也表现出压电和热电性质。由于分子中碳氟键的极性比碳氯键大，预期在热电性质方面具有优越性质，而且氟取代物的碳氟键能高，其化学稳定性要好于氯取代类似物。聚[3,3-双(氟甲基)氧杂环丁烷]的合成与聚[3,3-双(氯甲基)氧杂环丁烷]的制备类似，首先合成3,3-双(氟甲基)氧杂环丁烷，然后利用开环聚合反应得到该聚合物。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条