1.
Taking an oil soluble resin A with good stability as the main material, a temporary-bridge ahead fluid used in high permeability cement sand control technology was developed in the paper.
高渗透水泥防砂技术是一种全新的化学防砂技术,为防砂开辟了一条经济、高效的途径,但在进行高渗透水泥防砂施工时,水泥浆的侵入常会对油层造成污染甚至永久性的伤害,严重时会使防砂固井作业失败,油井丧失生产能力。
2.
The performance and capacity of sand control of e-mulsified diesel oil high permeability cement system were studied.
对乳化柴油高渗透水泥体系的综合性能和防砂能力进行了试验分析研究,结果表明,形成的水泥石能够达到良好的标准,文章采取的是先配置好稳定的乳化柴油溶液,再加入水泥和石英砂,促凝剂等各种水泥添加剂,最后获得了具有良好浆态性质和渗透率可调的渗透性水泥,凝固后其抗压强度达到6～8MPa,经一定处理后渗透率达到0。
4) cement leakage
骨水泥渗漏
1.
The cement leakage and the range depends on the injection stress ,the subsequent flow and the vascular egress in the vertebral body.
骨水泥的渗漏与否及渗漏的范围主要取决于骨水泥注射时的压力、骨水泥在椎体中的后续流动或者椎体中是否存在血管通道及其数量,因此通过减小骨水泥注射时的压力、增加注射时的阻力、阻挡其后续的流动或者封闭血管通道可以起到减少骨水泥渗漏的目的。
2.
The restorations of kyphosis was determined and cement leakage was observed.
比较2组手术前1d,手术后1d,1周,4周,8周,12周和24周测定疼痛视觉模拟评分和患者满意程度,测定后凸矫正率,观察骨水泥渗漏率。
6) high permeable cement slurry
高渗透水泥浆
1.
Study on rheological property of high permeable cement slurry under high temperature and high pressure;
高渗透水泥浆高温高压流变性研究
补充资料：骨水泥
分子式：
CAS号：
性质：用于骨科手术中的骨折固定、全膝及其他关节置换、人工关节固定、骨肿瘤刮除后的填塞等用途的聚甲基丙烯酸甲酯类高分子材料。为粉状与液态两包装，粉末为聚甲基丙烯酸甲酯及甲基丙烯酸甲酯-苯乙烯(或丙烯酸丁酯)共聚物，含少量的过氧化苯甲酰引发剂，液体为甲基丙烯酸甲酯单体，少量的氢醌，N,N′-二甲基对甲苯胺等。使用时将粉液混合，迅速搅拌，未固化前塞人髓腔，5～10min固化，能将人工关节的长柄固定于骨髓腔中，固化系放热反应，应避免周围组织热切；死，而且一些未参与聚合的单体亦会引起患者的生理反应，如血压下降心跳放慢等，注意减少单体用量。
CAS号：
性质：用于骨科手术中的骨折固定、全膝及其他关节置换、人工关节固定、骨肿瘤刮除后的填塞等用途的聚甲基丙烯酸甲酯类高分子材料。为粉状与液态两包装，粉末为聚甲基丙烯酸甲酯及甲基丙烯酸甲酯-苯乙烯(或丙烯酸丁酯)共聚物，含少量的过氧化苯甲酰引发剂，液体为甲基丙烯酸甲酯单体，少量的氢醌，N,N′-二甲基对甲苯胺等。使用时将粉液混合，迅速搅拌，未固化前塞人髓腔，5～10min固化，能将人工关节的长柄固定于骨髓腔中，固化系放热反应，应避免周围组织热切；死，而且一些未参与聚合的单体亦会引起患者的生理反应，如血压下降心跳放慢等，注意减少单体用量。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条