1) Magnetic hollow latex particles
磁性中空乳胶
2) hollow latex particles
中空乳胶粒
1.
Seeded emulsion polymerization was adopted to prepare hollow latex particles with moderate size and enough rigidity.
论文研究了搅拌强度、反应温度、羧基单体甲基丙烯酸的用量及加料方式、乳化剂用量及加料方式、交联单体用量、核壳层单体用量的比例、碱处理时间、温度和初始pH值等因素对乳液体系稳定性、中空乳胶粒粒径及其结构形态的影响,确定了最佳搅拌强度、最适宜反应温度、最佳核壳单体比、适宜乳化剂、交联剂、羧酸单体用量及适宜加料方式和最佳碱处理条件。
2.
Polymer emulsion with hollow latex particles, which is film-formable under room temperature and can be cross-linked under high temperature, was prepared by core-shell emulsion polymerization under low emulsifier condition.
首先以甲基丙烯酸甲酯(MMA)、甲基丙烯酸(MAA)和丙烯酸丁酯(BA)为共聚单体制备种子乳液;并在种子乳液基础上以MAA、MMA和二乙烯基苯(DVB)为单体进行聚合,制成带羧基的核乳胶粒;然后以苯乙烯(St)、MAA、BA以及DVB为共聚单体制备交联的共聚物;随后在最外层包覆BA和甲基丙烯酸缩水甘油酯(GMA)的共聚物;最后通过对其进行碱处理,制得含有功能性基团的中空乳胶粒。
3.
In this paper, emulsion polymerization was adopted to prepare hollow latex particles with moderate size and enough rigidity.
论文研究了搅拌强度、反应温度、加料方式、乳化剂用量及其加料方式、交联单体用量、碱处理时间等因素对乳液体系稳定性、中空乳胶粒粒径分布及其结构形态的影响。
3) hollow latex particle
中空乳胶粒子
1.
The preparation in osmotic swelling and the application performances of hollow latex particle in electrophoretic display ware mainly discussed in this study.
本文研究的主要内容为以渗透溶涨法制备中空乳胶粒子,并研究其在电泳显示方面的应用性能。
4) Magnetic hollow spheres
磁性中空球
5) hollow polymer particle
中空结构乳胶粒子
6) control latex
空白胶乳
补充资料:磁性
分子式:
CAS号:
性质:物质和磁场相互作用的性质。按照相互作用的不同,分成顺磁性、反磁性、铁磁性、反铁磁性等几种类型。与物质的电子结构、有无不成对电子、磁子间相互作用、晶体结构等物质和磁场相互作用的性质。按照相互作用的不同,分成顺磁性、反磁性、铁磁性、反铁磁性等几种类型。与物质的电子结构、有无不成对电子、磁子间相互作用、晶体结构等有关。有关。
CAS号:
性质:物质和磁场相互作用的性质。按照相互作用的不同,分成顺磁性、反磁性、铁磁性、反铁磁性等几种类型。与物质的电子结构、有无不成对电子、磁子间相互作用、晶体结构等物质和磁场相互作用的性质。按照相互作用的不同,分成顺磁性、反磁性、铁磁性、反铁磁性等几种类型。与物质的电子结构、有无不成对电子、磁子间相互作用、晶体结构等有关。有关。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条