1) iron-nickel-based cemented carbide
铁镍基硬质合金
2) Hard Nickel Cast Iron
硬镍合金铸铁
3) iron-nickel alloy
铁镍基合金
1.
The microstructure and composition distribution of the iron-nickel alloy lined layer in a composite steel pipe produced by centrifugal-SHS process were invest igated.
研究了铝热-离心法制备的铁镍基合金内衬复合钢管的显微结构,分析了内衬层沿径向的成分分布。
2.
The microstructure of the iron-nickel alloy lined layer in a composite pipe produced by centrifugal-thermit process was investigated The radial composition distribution of the alloying elements in the lined layer was analyzed The results show that the iron-nickel alloy was composes of austenite and ferrite A martensitic transition region ca.
研究了铝热 -离心法制备的铁镍基合金内衬复合钢管的组织结构 ,分析了内衬层沿径向的成分分布。
4) nickel-cemented carbide
镍粘结硬质合金
5) nickel hardfacing alloy
高硬度镍基合金
6) Ni based hardfacing alloy
镍基硬面合金
补充资料：镍硬铸铁
分子式：
CAS号：
性质：以镍铬为主的白口铸铁。镍硬1号含（%）：C3.0～3.6, Si0.3～0.5, Mn0.3～0.7, Ni3.3～4.8, Cr1.5～2.6; 镍硬2号含（%）：C≤2.9,Si 0.3～0.5, Mn0.3～0.7, Ni3.3～5.0, Cr1.4～2.4; 镍硬4号含（%）：C2.6～3.2, Si1.8～2.0, Mn0.4～0.6, Ni5.0～6.5, Cr8.0～9.0。它们均以马氏体为主，尚有一定的贝氏体和奥氏体。它们的硬度较高，镍硬1号为HRC53～61，镍硬2号为HRC52～59，镍硬4号为HRC53～63。镍硬铸铁最好用电炉熔化，便于控制成分和浇注温度，通常均需进行热处理。镍硬铸铁广泛用于低抗磨损，如轧辊、衬板、磨煤机的磨辊和磨环、输送管道、杂质泵过流部件等。
CAS号：
性质：以镍铬为主的白口铸铁。镍硬1号含（%）：C3.0～3.6, Si0.3～0.5, Mn0.3～0.7, Ni3.3～4.8, Cr1.5～2.6; 镍硬2号含（%）：C≤2.9,Si 0.3～0.5, Mn0.3～0.7, Ni3.3～5.0, Cr1.4～2.4; 镍硬4号含（%）：C2.6～3.2, Si1.8～2.0, Mn0.4～0.6, Ni5.0～6.5, Cr8.0～9.0。它们均以马氏体为主，尚有一定的贝氏体和奥氏体。它们的硬度较高，镍硬1号为HRC53～61，镍硬2号为HRC52～59，镍硬4号为HRC53～63。镍硬铸铁最好用电炉熔化，便于控制成分和浇注温度，通常均需进行热处理。镍硬铸铁广泛用于低抗磨损，如轧辊、衬板、磨煤机的磨辊和磨环、输送管道、杂质泵过流部件等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条