1) nano-silica/polyacrylate resin
纳米SiO_2改性聚丙烯酸树脂
2) modification of acrylic resin
聚丙烯酸树脂改性
3) modified acrylics
改性聚丙烯酸系树脂
4) modified acrylic resin
改性丙烯酸树脂
1.
A modified acrylic resin leather finishing agent was synthesised by adding acrylic acid and N-hydroxymethylacrylamide to butaylacrylate-acrylonitrite-vinylbenzene system with semi-continous polymerization proces
以丙烯酸丁酯为软单体，以丙烯腈和苯乙烯为硬单体，加入丙烯酸和Ｎ－ 羟甲基丙烯酰胺改性剂，通过半连续乳液聚合法合成了改性丙烯酸树脂皮革涂饰剂，并讨论了影响乳液性能的一些因素。
2.
An acrylic copolymer with pendant hydroxyl was synthesized by using acrylic monomers in methyl ethyl ketone, and the synthesized acrylic copolymer was modified by the half adduct of isophorone di-isocyanate and β-hydroxyethyl methacrylate to prepare the modified acrylic resin containing both N, A'-dimethyl amino group and vinyl group applicable for UV curable cathodic electrophoretic paint.
考察了催化剂、反应温度、反应时间等对IPDI半加成物的合成及IPDI半加成物改性丙烯酸树脂反应的影响;研究了酸中和后树脂水分散性的影响因素和电泳工艺参数对电泳漆膜厚度和外观的影响;并对漆膜光固化速度和固化膜性能的影响因素进行了探讨。
6) acrylated alkyd resin
丙烯酸酯改性醇酸树脂
补充资料：聚丙烯酸树脂Ⅱ
【通用名称】
聚丙烯酸树脂Ⅱ
【其他名称】
聚丙烯酸树脂Ⅱ 聚丙烯酸树脂Ⅱ 拼音名：Jubingxisuan Shuzhi Ⅱ 英文名：Polyacrylic Resin Ⅱ 书页号：2000年版二部－993 本品为甲基丙烯酸与甲基丙烯酸甲酯以50:50的比例共聚而得。
【性状】
本品为白色条状物或粉末，在乙醇中易结块。 本品（如为条状物断成长约1cm ，粉末则不经研磨）在温乙醇中 1小时内溶解，在 水中不溶。 黏度 取本品6.0g，加乙醇 100ml，微温使溶解，用旋转式黏度计，依法测定（附 录Ⅵ G 第二法），在25℃时的动力黏度不得过50Pa·s。 酸值 取本品约0.5g，精密称定，置250ml 锥形瓶中，加75％中性乙醇（对酚酞指 示液显中性）25ml，微温使溶解，放冷，精密滴加氢氧化钠滴定液(0.1mol/L)15ml，加 氯化钠5g与水10ml，用氢氧化钠滴定液(0.1mol/L)继续滴定至粉红色持续30秒钟不褪。 本品的酸值（附录Ⅶ H），按干燥品计算，应为300～330。
【鉴别】
本品的红外光吸收图谱应与对照品的图谱一致。
【检查】
酸度 取本品3g，加pH值约为7 的75％乙醇100ml,微温使溶解，放冷， 依法测定（附录Ⅵ H），pH值应为4.0 ～6.0 。 干燥失重 取本品，在110℃干燥至恒重，减失重量不得过10.0％（附录Ⅷ L）。 重金属 取本品1.0g，依法检查（附录Ⅷ H第二法），含重金属不得过百万分之三 十。 砷盐 取本品1.0g，置150ml 锥形瓶中，加硫酸5ml ，加热完全炭化后，逐滴加入 浓过氧化氢溶液（如发生大量泡沫，停止加热并旋锥形瓶，防止未反应物在瓶底结块） 直至溶液无色。放冷，小心加水10ml，再加热至三氧化硫气体出现，放冷，缓缓加水适 量使成28ml，依法检查（附录Ⅷ J），应符合规定（0.0002％）。
【类别】
药用辅料。
【贮藏】
密封，在阴凉处保存。