1) fore-solution treatment
预先固溶处理
3) solution heat treatment
固溶处理
1.
The effects of solution heat treatment processes on the microstructure and mechanical properties of the spray deposited 7090/SiC_P composite were investigated.
研究了固溶处理工艺对喷射沉积7090/SiC_p铝基复合材料的显微组织和力学性能的影响。
2.
It is thereby shown that the spinning and bulging forming can be done successfully, when taking four paths stepped spinning process, non-completed solution heat treatment (460℃±10℃ 30 min quenching by water) before spinning and completed solution heat treatment (515℃±10℃ 15 min quenching by water) before bulging for 6061.
结果表明,以6061铝合金为材质,采取4道次错距强旋成形工艺以及旋压前进行不完全固溶处理[(460±10)℃ 30 min、水淬]、胀形前进行完全固溶处理[(515±10)℃15 min、水淬],可确保旋压及胀形过程顺利进行,壳体的凹槽形状、尺寸精度、力学性能以及表面质量均可得到有效的保证。
3.
To dissolve the intermetallics which precipitated from the matrix of the layer, a solution heat treatment is conducted.
采用双层辉光离子渗金属技术 ,首先在低碳钢表面渗入合金元素钨、钼 ;然后作固溶处理 ,使金属间化合物溶于基体中 ;接着渗碳 ,使合金层内形成大量弥散、均匀、细小的合金碳化物。
4) solution treatment
固溶处理
1.
Effect of solution treatment on the microstructure and properties of 0Cr17Mn11Mo3N steel prepared by metal powder injection molding;
固溶处理对注射成形0Cr17Mn11Mo3N钢组织性能的影响
2.
Effects of solution treatment on the microstructures and mechanical properties of Al-1.5Si-1.2Mg-0.6Cu-0.3Mn aluminum alloy sheets;
固溶处理对Al-1.5Si-1.2Mg-0.6Cu-0.3Mn铝合金组织性能的影响
3.
Effect of solution treatment on microstructure and properties of 7B04 aluminum alloy;
固溶处理对7B04铝合金组织和性能的影响
5) solid solution treatment
固溶处理
1.
Effect of solid solution treatment on microstructure and properties of MIM Cr17Mn11Mo3N stainless steel;
固溶处理对注射成型Cr17Mn11Mo3N不锈钢组织性能的影响
2.
Effects of Y addition and solid solution treatment on microstructure and mechanical properties of AM60 magnesium alloys;
稀土Y及固溶处理对AM60镁合金组织和力学性能的影响
3.
Effect of the cooling rate during solid solution treatment on the properties of 1420 alloy;
固溶处理冷却速度对1420合金性能的影响
6) solid solution
固溶处理
1.
Morphology Transformation of Eutectic Silicon in Al-Si Alloy during Solid Solution Treatment;
铝硅合金中共晶硅在固溶处理时的形态转变
2.
Effect of Solid Solution and Aging on Structure and Properties of 17-4PH Precipitation-Hardening Stainless Steel;
固溶处理和时效对17-4PH沉淀硬化不锈钢组织性能的影响
3.
Effect of Cu Content on the Behavior of Solid Solution Treated Al-Mg-Si Alloy;
Cu含量对Al-Mg-Si合金固溶处理行为的影响