Stress corrosion crack (SCC) susceptibility of titanium alloy TA7 in methanol and hydrochloric acid-methanol solutions was studied by slow strain rate tensile test (SSRT), SEM and optical photography.
采用慢应变速率试验,辅以扫描电镜、金相观察等分析测试技术,研究了钛合金TA7在甲醇、盐酸-甲醇溶液中的应力腐蚀敏感性。
2.
The experimental results show that TC4 is possessed of SCC susceptibility in methanol solution, and addition of methanol solution to hydrochloric acid methanol solution can greatly improved the SCC susceptibility of TC4 alloy.
采用慢应变速率试验,辅以扫描电镜、金相观察等分析测试技术,研究了钛合金TC4在甲醇、盐酸-甲醇溶液中的应力腐蚀敏感性。
3.
The effects of methanol solution concentration and flow rate on the cell transient response are reported in this paper.
报道了甲醇溶液浓度和流量的影响。
3) methanol solution of sodium methylate
甲醇钠甲醇溶液
1.
Solid sodium methylate(>98%) was manufactured from methanol solution of sodium methylate(27%～31%).
以甲醇钠甲醇溶液 (2 7%～ 31% )为原料制备固体甲醇钠 (>98% ) ,研究了溶媒种类、配比、真空度、温度控制对产品质量的影响。
4) methanol/water solution
甲醇-水溶液
6) methanol/water mixture
甲醇/水溶液
1.
In this paper the composite pervaporation membranes were prepared,and the performance has been studied in the separation of methanol/water mixtures.
本论文主要的研究内容是制备用于分离甲醇/水溶液优先透水渗透汽化复合膜,本研究是在制备了PVA缩甲醛膜(PVA)、AA和AN的共聚膜(PAA-Co-AN)、纳米SiO_2改性的AA和AN共聚膜(PAA-Co-AN(SiO_2))、PVA/PAA-Co-AN/PVA三层结构复合膜(PVA/PAA-Co-AN/PVA)基础上,又制备出水优先透过的三层夹心复合渗透汽化膜PVA/PAA-Co-AN(SiO_2)/PVA用所制得的各种膜对不同浓度的甲醇/水溶液在不同温度下进行渗透汽化实验,对所得结果进行比较,结果发现PVA/PAA-Co-PAN(SiO_2)/PVA三层结构复合膜的分离性能较好。
补充资料：被动
①待外力推动而行动（跟‘主动’相对）：工作要主动，不要～。②不能造成有利局面使事情按照自己的意图进行（跟‘主动’相对）：由于事先考虑不周，事情搞得很～。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条