1) crumb rubber mortar
橡胶集料砂浆
1.
In this paper, the direct tensile strength of crumb rubber mortar was studied by this test piece.
本文还通过使用这种试件测量橡胶集料砂浆的直接抗拉强度,通过对单位体积砂浆分别掺入0、50、100、150kg的橡胶,发现橡胶的掺入会显著减小其直接抗拉强度,但可以明显改善弹性模量和变形性能,说明橡胶加入可以降低弹模,增大变形,具有较好的抗裂性能。
2) crumb rubber mortar(CRM)
橡胶细集料砂浆
3) crumb rubber dry-mixing mortar
橡胶集料干粉砂浆
1.
In this paper,different compound ratio of the crumb rubber dry-mixing mortar,waste rubber aggregate as being lightweight aggregate,redispersible polymer powders lignocelluloses,methylcellulose etc,were compounded,based on the research of their main properties such as flexibility,bulk density,bonding strength and thermal conductivity.
以废旧橡胶集料作为轻质保温材料,结合可再分散胶粉、木质纤维和甲基纤维素醚等制备了橡胶集料干粉砂浆,对其柔韧性、容重、粘结强度和导热系数等性能进行了研究。
4) rubberized mortar
橡胶砂浆
1.
Properties of anti-cracking of rubberized mortar were studied at plastic stage and hard stage by the method of board and ring devices respectively.
分别用平板法及圆环法测试研究了不同代砂率的橡胶砂浆在塑性阶段及硬化早期阶段的收缩开裂性能。
5) rubber mortar
橡胶粉砂浆
1.
Predicating properties of rubber mortar based on BP neural network;
基于BP神经网络的橡胶粉砂浆性能的预测
2.
The thermal performance of the wall effected by plastering rubber mortar is analysed.
分析计算了橡胶粉砂浆抹面对砌块墙体热工性能的影响。
6) crumb rubber
橡胶集料
1.
The research progress of Portland cement concrete containing crumb rubber;
橡胶集料混凝土研究进展综述
2.
The compressive and flexural behavior of crumb rubber concrete(CRC) was investigated with the content of crumb rubber ranging from 50/0 to 150/0 by volume.
针对橡胶集料混凝土的抗压及抗弯性能,在500/~1500/橡胶集料体积掺量下进行立方体抗压强度以及单轴受压应力-应变全曲线试验,并利用动态应变仪测量了4点弯曲状态下的拉应变。
3.
This article presents an experimental analysis on CRC with high crumb rubber volume incorporation, which is firstly mixed using domestically produced materials.
橡胶集料混凝土作为一种新型混凝土材料,具有低弹性模量、大变形、高阻尼、能量耗散多及良好的抗裂性等特点,引起混凝土业界的广泛兴趣。
补充资料：橡胶模具、橡胶压模、橡胶硫化模
分子式：
CAS号：
性质：又称橡胶模具、橡胶压模、橡胶硫化模。用于压制橡胶产品的金属模型。一般用钢材(如45号钢)按图纸要求经机械加工而制得，并经热处理以提高其硬度及耐磨性。模具型腔与产品结构相同，型腔尺寸必须考虑不同橡胶的收缩率，在产品尺寸基础上进行放大或缩小，方可得到合适的产品尺寸。模具从工艺操作考虑还要设置流胶槽、启模口、定位销等。
CAS号：
性质：又称橡胶模具、橡胶压模、橡胶硫化模。用于压制橡胶产品的金属模型。一般用钢材(如45号钢)按图纸要求经机械加工而制得，并经热处理以提高其硬度及耐磨性。模具型腔与产品结构相同，型腔尺寸必须考虑不同橡胶的收缩率，在产品尺寸基础上进行放大或缩小，方可得到合适的产品尺寸。模具从工艺操作考虑还要设置流胶槽、启模口、定位销等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条