1) PANI/HPC composites
PANI/HPC复合材料
2) PANI/Cu composites
PANI/Cu复合材料
3) PANI/CNTs composites
PANI/CNTs复合材料
4) PANI/V_2O_5 hybrid materials
PANI/V_2O_5杂化材料
1.
Organic-inorganic PANI/V_2O_5 hybrid materials of V_2O_5 with polyaniline(PANI) were prepared from V_2O_5 gel precursor and aniline monomer by in situ oxidative polymerization of aniline in the solution.
利用V_2O_5凝胶前驱体和苯胺单体在溶液中原位氧化聚合制备了V_2O_5和聚苯胺(PANI)的有机-无机PANI/V_2O_5杂化材料,分别利用X-射线衍射(XRD)、热分析(TG-DTA)、扫描电镜(SEM)、红外光谱(FT-IR)技术对杂化材料进行了表征。
5) (PSS/PANI)n composite film
(PSS/PANI)n复合膜
6) PANI/C composite electrode
PANI/C复合电极
1.
The research progress in polyaniline(PANI) electrode material of supercapacitor was summarized from the aspects of acid doped PANI electrode,Li salt doped PANI electrode,PANI/C composite electrode and hybrid capacitor.
从酸掺杂聚苯胺(PANI)电极、锂盐掺杂PANI电极、PANI/C复合电极及混合电容器等方面,对超级电容器用PANI电极材料的研究进展进行了总结,对其发展前景做出了展望。
补充资料：Pan
分子式：C15H11N3O
分子量：249.28
CAS号：85-85-8
性质：橙红色无定形粉末。熔点141℃，溶于甲醇、乙醇、苯、醚、氯仿和热稀碱液，不溶于水。溶液在pH12以上时呈粉红色，在弱酸中呈橙红色，在浓硫酸中呈紫色。其金属络合物呈粉红色或红色。
制备方法：由2-氨基吡啶经重氮化后，与2-萘酚偶合而得。将无水乙醇与金属钠反应生成乙醇钠，然后加入2-氨基吡啶的乙醇溶液，通入亚硝酸乙酯蒸气于45-50℃反应。能毕，保温8小时，过滤出重氮盐用乙醚洗涤。将重氮盐加入2-萘酚的乙醇溶液中，在45-50℃通入二氧化碳进行偶合反应，6小时后过滤出结晶，用蒸馏水洗涤后再用乙醇重结晶，干燥即为成品。
用途：该品为络合指标剂。
分子量：249.28
CAS号：85-85-8
性质：橙红色无定形粉末。熔点141℃，溶于甲醇、乙醇、苯、醚、氯仿和热稀碱液，不溶于水。溶液在pH12以上时呈粉红色，在弱酸中呈橙红色，在浓硫酸中呈紫色。其金属络合物呈粉红色或红色。
制备方法：由2-氨基吡啶经重氮化后，与2-萘酚偶合而得。将无水乙醇与金属钠反应生成乙醇钠，然后加入2-氨基吡啶的乙醇溶液，通入亚硝酸乙酯蒸气于45-50℃反应。能毕，保温8小时，过滤出重氮盐用乙醚洗涤。将重氮盐加入2-萘酚的乙醇溶液中，在45-50℃通入二氧化碳进行偶合反应，6小时后过滤出结晶，用蒸馏水洗涤后再用乙醇重结晶，干燥即为成品。
用途：该品为络合指标剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条