1) sol-dip-coating method
溶胶浸渍提拉法
1.
In this study, tungsten trioxide EC films were successfully prepared via sol-dip-coating method and sol-electrophoretic method using stable tungsten trioxide sol synthesized by tungstic acid.
溶胶浸渍提拉法制备的氧化钨薄膜,在500℃保温3h的热处理温度下表面非常平整,形成了纳米尺度的晶粒,薄膜具有较好的着色-褪色性能,薄膜的循环伏安特性稳定,离子的注入与抽出过程可逆性好,薄膜的着色态与褪色态的最大透光率差值出现在750nm波长处,约为45%,具有较好的光线调节能力。
2) sol-gel-dipping process
溶胶-凝胶-浸渍提拉法
1.
With thiourea as the source substance of S,with Titanium tetrabutoxide(Ti(OC4H9)4 as the precursor of titanium dioxide and with honeycomb ceramics as carriers,S-TiO2 films were prepared by a modified sol-gel-dipping process.
以硫脲为S的源物质,以钛酸丁酯为TiO2的前驱体,以蜂窝陶瓷为载体,采用改进的溶胶-凝胶-浸渍提拉法制备Ti1-xSxO2薄膜,探讨热处理温度、S掺杂量及涂膜等工艺条件对Ti1-xSxO2薄膜的光催化活性的影响。
3) dip-coating method
浸渍-提拉法
1.
A study on gas sensitivity of WO_3 films prepared by dip-coating method;
浸渍-提拉法制备WO_3薄膜的气敏性能研究
4) dip-coating method
浸渍提拉法
1.
Piezoelectric and ferroelectric polymer film of PVDF was successfully prepared by dip-coating method.
采用溶液浸渍提拉法制备了β型PVDF压电聚合物薄膜,采用X衍射、扫描电镜等手段测定了PVDF薄膜的物相结构,结晶形态及薄膜厚度等。
5) dip-coating
浸渍-提拉法
1.
Methods The dip-coating method were applied to fabricated an alumina coating on the surface of the metal based honeycomb substrates.
方法采用浸渍-提拉法(dip-coating)在所选的金属基体材料上制备氧化铝涂层,所用的载体是用自制设备制作的金属蜂窝状载体。
2.
After concentration, the dip-coating method were applied to fabricated an alumina coating on the surface of the metal based honeycomb substrates.
将氧化铝溶胶进行一定的浓缩，采用浸渍-提拉法在所选的金属基体材料上制备氧化铝涂层，经过溶胶-凝胶转变、干燥和热处理等过程在金属表面得到多孔氧化铝涂层，所用的载体是用自制设备制作的金属蜂窝状载体。
6) sol-dipping method
溶胶-浸渍法
1.
The reaction kinetics and mechanism of oxidation reaction of SiO_2 coating/3-D braided carbon fiber prepared by the sol-dipping method were studied systemly through XRD,SEM,isothermal weight-loss and non-isothermal TG-DTG methods.
采用溶胶-浸渍法,在三维碳纤维编织体的纤维表面涂覆SiO2涂层,通过XRD、SEM、等温氧化失重和非等温TG-DTG等测试手段研究了制备方法对涂层完整性的影响,并对涂层/编织体材料(CB)氧化反应的动力学和机理进行了系统研究。
2.
The SiO2 coating on 3-D braided carbon fiber was prepared by the sol-dipping method.
采用溶胶-浸渍法,成功地在三维编织碳纤维的纤维表面涂覆SiO2,并通过碳热还原反应制得厚度约为0。
3.
The SiO2 coating on 3-D carbon fiber braids was prepared by the sol-dipping method.
采用溶胶-浸渍法,在三维碳纤维编织体的纤维表面涂覆SiO_2涂层。
补充资料：溶胶
分子式：
CAS号：
性质：又称溶胶。是难溶于水的固体物质分散在液体中的胶态分散体系。是高度分散的多相体系。分散相的粒子大小在10-9～10-7m范围内，不稳定，有自动聚结沉淀的趋势。根据分散介质的不同，可分为固溶胶，液溶胶和气溶胶三类。根据与液体分散介质的关系可分为亲液溶胶和憎液溶胶两类。溶胶有特征的丁铎尔效应，在超显微镜下可观察到布朗运动。一些溶胶粒子可带电，通电时发生电泳现象。溶胶-凝胶技术是制备非晶态固体的重要方法。
CAS号：
性质：又称溶胶。是难溶于水的固体物质分散在液体中的胶态分散体系。是高度分散的多相体系。分散相的粒子大小在10-9～10-7m范围内，不稳定，有自动聚结沉淀的趋势。根据分散介质的不同，可分为固溶胶，液溶胶和气溶胶三类。根据与液体分散介质的关系可分为亲液溶胶和憎液溶胶两类。溶胶有特征的丁铎尔效应，在超显微镜下可观察到布朗运动。一些溶胶粒子可带电，通电时发生电泳现象。溶胶-凝胶技术是制备非晶态固体的重要方法。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条