1) modified zeolite powders
改性沸石粉
1.
Considering material costs and meanwhile ensureing higher cadmium(Ⅱ) removing rate by modified zeolite powders,the optimum preparation technology is modified time 12 h,mixture ratio of chitosan and zeolite powder 1:40,sodium hydroxide concentration 2 mol·L~(-1).
本文采用壳聚糖和氢氧化钠对天然沸石粉进行改性,并在不同改性时间、沸石粉与壳聚糖的配比和氢氧化钠浓度的条件下制备了新型改性沸石粉吸附材料;采用吸附-混凝的处理方法,以微污染源水中镉(Ⅱ)的去除率为评价指标,确定了改性沸石粉的较佳改性条件。
2) modified powdered zeolite
改性粉末沸石
1.
The combined use of modified powdered zeolite and ultrafiltration membrane has synergistic effect on organics removal.
采用改性粉末沸石对超滤膜表面进行预涂层,研究了预涂层工艺对改善膜通量的作用与机理,结果表明:沸石经酸法改性后,比表面积增加,表面负电性降低,是合适的涂层物质。
3) modified zeolite
改性沸石
1.
Removing ammonia nitrogen from sewage by modified zeolite;
改性沸石处理含氨氮废水
2.
Experiment on polluted scenic reclaimed-water by modified zeolite and biofilm system;
改性沸石生物滤池处理中水景观污染水体实验研究
3.
Study of Property of PP/Modified Zeolite Composite;
PP/单甘酯改性沸石复合材料的研究
5) HCl modification zeolite
HCl改性沸石
1.
A novel compound barrier constructed with HCl modification zeolite and calcite was reported to control phosphorus and nitrogen release from sediments.
提出了HCl改性沸石和方解石复合覆盖控制底泥氮磷释放的新方法,利用摇床振荡试验和底泥氮磷释放控制模拟试验,设计了5种底泥处理方案,重点针对HCl改性沸石和方解石复合覆盖技术研究了其抑制底泥氮磷释放的效果及机理。
补充资料：4A沸石
分子式：
CAS号：
性质：又称Na12[(A1O2)12、(SiO2)12]27H2O 又称4A分子筛。白色固体颗粒。呈网络状结构，内含均匀小孔，孔径0.42nm，比表面积约为600m2/R，不溶于水和有机溶剂，能溶解于强碱和强酸。加热超过800℃时，重新结晶形成白硅石状的结构。有吸附水分，液体、气体及不饱和的有机物质。对钙离子有交换能力，理论交换能力为352CaCO3mg/g，一般为290～320mgCaCO3/g，白度≥95%，pH值10～11.5，表观密度0.3～0.5g/cm3，平均粒径为2μm，粒度分布≤4μm占85%以上。用作无磷洗涤剂的助剂，代替三聚磷酸钠；在石油和其他工业用作气体和液体的干燥、脱水净化等，也用作催化剂和软水剂。
CAS号：
性质：又称Na12[(A1O2)12、(SiO2)12]27H2O 又称4A分子筛。白色固体颗粒。呈网络状结构，内含均匀小孔，孔径0.42nm，比表面积约为600m2/R，不溶于水和有机溶剂，能溶解于强碱和强酸。加热超过800℃时，重新结晶形成白硅石状的结构。有吸附水分，液体、气体及不饱和的有机物质。对钙离子有交换能力，理论交换能力为352CaCO3mg/g，一般为290～320mgCaCO3/g，白度≥95%，pH值10～11.5，表观密度0.3～0.5g/cm3，平均粒径为2μm，粒度分布≤4μm占85%以上。用作无磷洗涤剂的助剂，代替三聚磷酸钠；在石油和其他工业用作气体和液体的干燥、脱水净化等，也用作催化剂和软水剂。