1) pure magnesium wire
纯镁丝材
1.
Consider for these characteristics of magnesium, there are some studies about cold drawing and mid-annealing techniques was performed on pure magnesium wires in this paper.
针对镁的这些特点本文研究了纯镁丝材的室温冷拉拔和中高温退火工艺过程,并将得到的丝材在模拟体液中进行腐蚀实验,研究了生理环境和晶粒尺寸对纯镁丝材的腐蚀影响。
2) magnesium wire
镁合金丝材
1.
The work-hardened magnesium wire online treatment process with high-density electropulse is investigated.
研究通过高能电脉冲对加工硬化的AZ31镁合金丝材进行在线处理,分析高能电脉冲作用下AZ31丝材力学性能、断口形貌及微观组织的变化机理,并与传统退火处理工艺进行了比较。
3) Magnesium
[英][mæɡ'ni:ziəm] [美][mæg'nizɪəm]
纯镁
1.
Modification and Alloying of High Purity Magnesium Surface with High Current Pulsed Electron Beam;
纯镁强流脉冲电子束表面改性及合金化研究
2.
Study on Formation of Magnesium-Hydroxyapatite Composite Coatings via Biomimetic Synthesizing;
仿生法制备纯镁/羟基磷灰石复合涂层的研究
3.
Preparation of Apatite Coating on Surface of Magnesium via Biomimetic Synthesizing;
通过仿生法在纯镁表面制备磷灰石涂层的研究
4) pure magnesium
纯镁
1.
Effects of Combined Forming on Structure and Mechanical Properties of Pure Magnesium;
联合成形工艺对纯镁的组织及性能的影响
2.
Effect of dicalcium phosphate dihydrate (DCPD) coating on the corrosion behavior of pure magnesium in simulated body solution;
二水磷酸氢钙(DCPD)涂层对纯镁在模拟体液中腐蚀行为的影响
3.
Mechanisms and microstructure of plastic deformation in pure magnesium;
纯镁塑变机理及其组织特征
5) pure Mg
纯镁
1.
Revamp and development of pure Mg desulphurization equipment system in No.1 Steel-making plant of WISCO;
第一炼钢厂纯镁脱硫设备系统的改造与开发
2.
The hot metal is very susceptible to resulfurization in the process of converter refining since adoption of the hot metal desulfurization process using pure Mg as desulfurizer in place of the hot metal desulfurization process with Mg-based powder at the hot metal desulfurizer of the No.
武钢第一炼钢厂将镁基喷粉铁水脱硫站改造成纯镁铁水脱硫工艺后因为脱硫后的渣少并且稀 ,不容易扒出 ,容易在转炉产生回硫。
3.
And the microstructure evolutions of pure Mg under compression were investigated in this study as a sample.
本文还以原位压缩过程中纯镁的微观组织演变的测试与分析为例,说明原位EBSD系统使用方法。
补充资料：镁铝锌系铸造镁合金
镁铝锌系铸造镁合金
magnesium-aluminium-zinc cast magnesium alloy series
mellUxlnx一zhuzao melhej一n镁铝锌系铸造镁合金(magnesium一alumini-um一Zine east magnesium alloy series)以铝、锌为主要合金化元素的铸造镁合金，可用于砂型和金属型铸造，也可用于压力铸造，具有良好的流动性和焊接性能，热裂倾向性低，但有较大的显微疏松倾向。 中国牌号ZM一5(7.5%一9.0%Al，0.15%一0.5%Mn，0.2%一0.8%Zn，Mg为余量)合金，ZM一10(9 .0%~1 0.2%AI，0.15%一0.5%Mn，0.2%一0.8%zn，Mg余量)合金。zM一5合金为镁铝锌系铸造镁合金的代表，相当于前苏联牌号的M月5合金。合金中杂质为铁、铜、镍、硅、钻等，根据需要可适量加些被。 铝是主要合金化元素并含有锌和锰，通过改变铝、锌含量可改变合金的力学性能、铸造性能及抗蚀性能。铝含量的增加能进一步改善合金的铸造性能和提高合金的强度，但使伸长率和抗腐蚀性能降低。加入少量的锌和锰能显著提高合金的抗蚀性能，还可以提高合金的强度。但锌含量增加会使合金的缩松倾向增加。ZM一5合金的铸态组织由固溶体叔Mg)为基体，沿它的晶界以不连续网状分布着y(Mg‘A13)相，以及分布在固溶体叔Mg)中的Mn一Ai化合物小质点所组成。热处理强化常采用两种规范:(1)淬火(T4):加热到370~380℃保温2一4h，再升温至415士5℃保温12一16h，然后在空气中冷却。(2)淬火时效(T6):淬火后再在175士5℃人工时效16h。ZM一5合金的力学性能见表1。 表1 zM一5合金的力学性能详 镁铝锌系铸造镁合金结晶间隔较大，充型能力良好，铸造工艺性能及物理常数见表2。表2 zM一s合金铸造工艺性能及物理常数}牛粉粉{字朴 镁铝锌系铸造镁合金能铸出外形和内腔形状复杂的铸件，加之镁合金在汽油、煤油、润滑油中很稳定，因而多用于航空工业的燃油系统和润滑系统。还可作为在受冲击载荷时能吸收大量能量的零部件及飞机着陆轮的轮毅。 (杨朴)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条