1) Glass encapsulation
糖玻璃化
2) hyaloidin
[haiə'lɔidin]
玻璃糖质
3) devitrified glass
脱玻化玻璃
1.
The results show that the glass imitation is a kind of opacified devitrified glass,mainly composed of SiO2 and Al2O3,subordinate alkali metal oxide of K,Na,Ca,Mg and other precipitate of calcium fluoride and calcium phosphate.
结果表明,该样品为乳浊的脱玻化玻璃,其主要成分为SiO2,其次为Al2O3,还含有K,Na,Ca,Mg碱金属氧化物以及乳浊剂的析出物氟化钙和磷酸钙。
4) glass toughening
玻璃钢化
6) Tempered Glass
钢化玻璃
1.
It has been discovered and demonstrated, via scanning electron microscope examination on 6 samples of broken glasses, that one important cause for the spontaneous breakage in tempered glass occurs as a result of the single-phase polycrystalline silicon particles, rather than simply the nickel sulfide (NiS) particles that are commonly recognized to be the main cause for the spontaneous breakage.
通过对 6 块玻璃自爆残片的电镜观察和成分分析,发现并证明了引起钢化玻璃自爆的主要原因不仅仅是传统认识中的硫化镍(NiS)微粒,很多情况是由单质硅微粒引起的。
2.
The causes of bend and distortion of tempered glass were discussed and some solutions were also suggested under any circumstances.
分析了钢化玻璃变形弯曲的原因,提出了各种情况下解决钢化变形的方法。
3.
Beijing Botanical Garden Exhibition Greenhouse uses point type glass curtain wall with imported tempered glass from French.
北京植物园展览温室采用点式玻璃幕墙 ,其钢化玻璃均从法国进口 ,抗弯强度和弹性模量能否采用现有的中国幕墙规范数值是个问题。
补充资料：糖玻璃
糖玻璃
在一般的情形下，糖及其凝结物是不会割伤人的。
因为糖的热融性决定了它的凝结物在常温下要冷却收缩，而在收缩的过程中，本来可能存在的锐利边缘会由于糖质的粘性和表面的张力而变得圆滑，除非在那样的凝结后用工具打磨出锋利的边缘，否则不应有可以割伤人的情况。
糖块的凝结状态大多是比较脆的，受力后很容易瓦解成小块，道具中常采用糖玻璃的原因正是糖本身所具有的这种特性所决定的。
当然，极端的情况也是有的，譬如糖块以高速擦过皮肤，仍可能对皮肤造成擦伤，但不会有刀割那样的严重情况发生，这是可以肯定的。
利用这一特性,在某些电影中就可以创造一些特技镜头,如用拳头打破玻璃.其实这块玻璃是糖做的玻璃
先配制饱和的砂糖溶液,倒入一些玉米糖浆和少量甘油同时稍微加热,不停搅拌,之后倒入模具.冷却之后就制作出了一块糖玻璃.它象普通的玻璃一样透明但比普通玻璃要脆弱.
说明：补充资料仅用于学习参考，请勿用于其它任何用途。