1) ASA core shell graft copolymer
ASA核壳接枝共聚物
2) chitosan copolymer
接枝壳聚糖共聚物
1.
The strengthening effect of chitosan copolymer on the physical properties of paper which was made of bleached softwood pulp and secondary fibers was studied in this paper,and the mechanism of strengthening effects of this chitosan copolymer was also discussed.
本文研究了不同工艺条件下接枝壳聚糖共聚物用在漂白针叶木浆和废纸浆中对纤维的增强作用。
4) CS-g-mPEG
壳聚糖-接枝-mPEG共聚物
5) grafted copolymer
接枝共聚物
1.
The results showed that the product was grafted copolymer of cellulose acetate and poly(actic acid),and poly(actic acid) side chains were detected in the copolymer.
为改善纤维素醋酸酯的热加工性能,以辛酸亚锡为催化剂,通过丙交酯的开环接枝聚合反应,制备了纤维素醋酸酯和聚乳酸接枝共聚物(CDA-g-PLA),利用FTIR、1H NMR、DSC、XRD和TG对其结构和性能进行表征。
2.
Polycarboxylate grafted copolymer used as superplasticizer was synthesized first through free radical copolymerization of acrylic acid and sodium allyl sulfonate to prepare copolymer containing carboxyl and sulfonic group,then esterification with polyethylene glycol monoalkyl ether.
通过丙烯酸与烯丙基磺酸钠的自由基共聚制备了含有羧基和磺酸基团的共聚物,然后将其与聚乙二醇单烷基醚进行酯化反应,合成了可用作高效减水剂的聚羧酸盐接枝共聚物。
3.
The grafted copolymers of methyl methacrylate (MMA) and CPE as the compotilizer of the PVC/CPE blends are discussed.
讨论了甲基丙烯酸甲酯（ＭＭＡ）与ＣＰＥ的接枝共聚物体系对ＰＶＣ－ＣＰＥ体系的增容作用。
6) graft copolymer
接枝共聚物
1.
Synthesis of polyaspartic acid graft copolymers and their scale inhibition and dispersion performance;
聚天冬氨酸接枝共聚物的合成及阻垢分散性能研究
2.
Synthesis and properties of CPP/VTES/St graft copolymer;
CPP/VTES/St接枝共聚物的合成与性能
3.
Water-swellable properties of amphiphilic chlorinated polyethylene graft copolymer;
双亲性氯化聚乙烯接枝共聚物的吸水膨胀性能
补充资料：AS
丙烯腈-苯乙烯共聚物是由丙烯腈和苯乙烯通过本体法、悬浮法或乳液法制得。透明或半透明的水白色颗航。相对密度1．06-1．08。折射率1．57。平衡吸水性0．66％。热变形温度82-105℃。具有高光泽、高透明、高冲击、良好的耐热性和机械性能。刚性大，具有较高的化学稳定性，耐水、耐油、耐酸、耐碱、耐醇类。溶于酮类溶剂和某些芳烃、氯代烃。耐候性中等，脆性较大。
拉伸强度 72-78MPa
冲击强度 2．1-2.5kJ/m2
洛氏硬度 R76-80
熔体指数 l. 4-3.3g/10min
说明：补充资料仅用于学习参考，请勿用于其它任何用途。