1) DMU (Dimethylol Urea)
二羟甲基脲;二甲醇脲
2) dihydroxyl-methyl-urea
二羟甲基脲
1.
Under the alkalescency condition, dihydroxyl-methyl-urea was synthesized by the addition reaction with urea and formaldehyde as materials.
在弱碱性条件下,以尿素和甲醛溶液为原料通过加成反应合成制备二羟甲基脲,利用FTIR、1HCMR对产物的结构进行了表征,用化学方法对其所含元素、羟甲基含量及游离甲醛含量进行分析。
3) dimethylolurea
二羟甲基脲
1.
The condensation polymer of dimethylolurea was synthesized from dimethylolurea by melt polycondensation and identified by FTIR,1 H NMR,13 C NMR and 15 N NMR.
以尿素和甲醛为原料,在碱性水溶液中合成了二羟甲基脲,利用FTIR,1HNMR和元素分析对其结构进行了表征。
4) dihydroxymethyl urea
二羟甲脲
1.
The comparison study shows that when urea and formaldehyde are prefabricated into dihydroxymethyl urea to modify phenol-formaldehyde resin, the usage of urea can be increased, the end point of reaction can be controlled more easily and the bin stability of resin is better in the course of modifying property of phenlol-formaldehyde resin by dihydroxymethyl urea than by urea.
通过用尿素和二羟甲脲改性酚醛树脂的对比试验,发现先将尿素和甲醛制成二羟甲脲后再加入酚醛树脂中参与合成,可增加尿素的用量,反应终点较易控制,树脂的贮存稳定性较好;苯酚与尿素的重量比为100∶75时,合成的二羟甲脲改性酚醛树脂用于压制胶合板,板的胶合强度仍达到国家标准GB9846 88中Ⅰ类胶合板的要求;最佳的热压工艺为:热压温度130℃、单位压力0 9MPa、热压时间0 9min/mm,固化条件比纯酚醛树脂低;由红外光谱分析可知,经二羟甲脲改性后形成了酚醛—脲醛共缩聚树脂;对原料成本概算,二羟甲脲改性的酚醛树脂比纯酚醛树脂降低了26
5) Oxymethurea
二羟甲基脲,Dimethylolurea
6) N,N'-dihydroxymethylurea
1,3-二羟甲基脲
补充资料：二羟甲基脲
分子式：CO(NHCH2OH)2
CAS号：
性质：无色结晶。熔点129～130℃。系尿素和甲醛反应制备氨基树脂的中间体之一，羟甲基具有反应活性。可由尿素和甲醛在盐类或碱性催化剂存在下制得，继续反应得到氨基树脂。
CAS号：
性质：无色结晶。熔点129～130℃。系尿素和甲醛反应制备氨基树脂的中间体之一，羟甲基具有反应活性。可由尿素和甲醛在盐类或碱性催化剂存在下制得，继续反应得到氨基树脂。