1) lead sesquioxide
三氧化二铅;偏高铅酸铅
2) lead metaplumbate
偏高铅酸铅
3) dilead trioxide
三氧化二铅
4) metaplumbic acid
偏高铅酸
5) plumbous metaplumbate
偏铅酸铅
6) PbO2
二氧化铅
1.
The characterizations of Ti/SnO2+Sb2O3/PbO2 anodes with SnO2+Sb2O3 as an intermediate layer obtained by way of a polymeric precursor, and using ethylene glycol, ethanol and n-butanol for different precursor solvents were studied.
研究了以乙二醇与柠檬酸反应制得的乙二醇柠檬酸酯溶液、乙二醇、乙醇、正丁醇为前驱体溶剂制备的锡锑中间层对Ti/SnO2+Sb2O3/PbO2电极性能的影响,用XRD、ESEM对不同前驱体制备的锡锑中间层和对应的二氧化铅活性层进行了表征,并用极化曲线法和阳极寿命快速检测法比较了不同前驱体对Ti/SnO2+Sb2O3/PbO2电极的阳极寿命和在1。
2.
During electrodepositing pure lead dioxide, the electrocatalytic activity of PbO2 electrodes, as well as their stability, can often be considerably enhanced by the incorporation of some foreign ions or fine particles added to the electrodeposition solution.
二氧化铅作为阳极由于具有高的催化活性、高的析氧过电位和化学惰性而受到关注。
补充资料：三氧化二铅
分子式：Pb2O3
CAS号：
性质：红黄色或绿棕色粉状物。不溶于冷水或氢氧化钾溶液。可被浓酸分解为二氧化铅和氧化铅。370℃左右放出氧，余留下四氧化三铅，约530℃左右时余留下氧化铅。在热水中徐徐分解。可将氧化铅溶于氢氧化钠，然后通入臭氧氧化制得。用于制取其他铅的氧化物。
CAS号：
性质：红黄色或绿棕色粉状物。不溶于冷水或氢氧化钾溶液。可被浓酸分解为二氧化铅和氧化铅。370℃左右放出氧，余留下四氧化三铅，约530℃左右时余留下氧化铅。在热水中徐徐分解。可将氧化铅溶于氢氧化钠，然后通入臭氧氧化制得。用于制取其他铅的氧化物。