1) VANADIZING IN THE SALT BATH WITH LOW CONTENT OF BORAX
低硼砂盐浴渗钒
3) borate bath vanadatizing
盐浴渗钒
1.
Application of borate bath vanadatizing in enhancing tooling and die life;
盐浴渗钒在工模具上的应用
4) borax bath
硼砂盐浴
1.
The influece of reducer on coating of Cr12MoV steel was studied by TD process using a borax bath.
采用硼砂盐浴的方法进行TD处理实验,研究了还原剂对Cr12MoV钢TD处理的影响。
5) TD salt-bath vanadizing treatment
TD盐浴渗钒处理
1.
The TD salt-bath vanadizing treatment of the Cr12MoV steel was investigated.
对Cr12MoV钢制模具表面TD盐浴渗钒处理后的硬化层进行了研究,结果表明:Cr12MoV钢经980℃保温5h后油淬和180℃×2h回火的TD盐浴渗钒处理后,可以形成由含V和C的化合物组成的厚约为11。
6) low temperature salt bath chromizing
低温盐浴渗铬
1.
The results showed that a chromized layer with good wear resistance could be gained in steel 45 by low temperature salt bath chromizing.
研究了 45钢低温盐浴渗铬工艺 ,分析了渗铬层的金相组织和相结构 ,测量了渗层厚度、渗层硬度及铬浓度分布 ,并进行了渗铬层的耐磨试验。
2.
The microstructure ,phase make up,chromium thickness,microhardness and corroding resistance of low temperature salt bath chromizing layers of steel Q235,45 and T10 are contrasted.
通过 Q2 35钢、45钢、T1 0钢低温盐浴渗铬层的金相组织、相结构、厚度、铬浓度、显微硬度和耐蚀性的对比 ,表明碳含量越高 ,铬碳化合物层越厚 ,显微硬度越高 ,耐蚀性越好。
3.
Immediate quenching and tempering process of steel T10 after low temperature salt bath chromizing was studied.
研究了 T10钢在低温盐浴渗铬后直接淬火并回火工艺。