1) upsetting barrel die
镦球模
2) ball heading
钢球镦锻
3) hot-forging dies
热镦模
1.
The boriding in vacuum ion liquid and gaseouse phases for hot-forging dies was introduced, the organic bleed is B(OCH3)3 made by oneself which is non-toxic and non-toxic and non-corrosiveness.
介绍了用自制的无毒无腐蚀的有机渗硼剂——硼酸三甲酯对排气阀热镦模进行真空离子液-气相渗硼,经检测,整个化合物层和扩散层中含有B和Fe2B,并呈高度弥散分布状态,起到了抗重载热冲击、抗热磨损、抗反复低周循环热疲劳的良好作用,能大大提高热镦模的使用寿命。
4) dieless upsetting
无模镦粗
1.
It has been put forward by experiment that the variation of wall thickness of tube is in directly propor-tion to outer-diameter ,inter-diameter,and (Rs-variation of tube area) during tube dieless upsetting.
对管材无模镦粗变形时壁厚变化进行了实验研究。
2.
In this paper, velocity field and variation of wall thickness are studiedtheoretically during tube dieless upsetting.
对管材无模镦粗变形速度场及壁厚变化规律进行了理论研究。
5) upsetting die
镦粗模
1.
In the present paper, the transient temperature of the surface on the upsetting die and its inside has been measured with the film thermocouples developed by authors.
采用自制的薄膜热电偶测定镦粗模具工作时表面和内部的瞬态温度，分析它的分布特点及热影响区的范围，建立锻模的温度分布函数，论述锻模瞬态温度波形的时域、频域特性及传递规律，总结出锻模透热深度与热冲击信号的谐波频率密切相关的重要结论，为锻模的热应力分析、热强度理论的建立及表面改性措施的采取提供一些基础性数据和理论根据。
6) electro-upsetting die
电镦模具
补充资料：自动冷镦机、多工位螺栓自动冷镦机
| |||||||
主要参数内容 | 国际先进 | 国内先进 | 国内一般 | 国内落后 | 评定方法及说明 | ||
（一）加工精度 | 参照GB9166-88、JB/T3053-91 | ||||||
1、冲头夹持器模孔中心线对夹持器后支承面的垂直度（mm） 在100长度上 | 0.008 | 0.01 | 0.015 | ＞0.015 | |||
2、凹模座模孔中心线对凹模后座支承面的垂直度（mm） 在100长度上 | 0.008 | 0.01 | 0.015 | ＞0.015 | |||
3、冲头夹持器模孔中心线对滑块行程的平行度（mm） 在100行程上 | 0.016 | 0.02 | 0.02 | ＞0.02 | |||
4、滑块行程对机身上与凹模座贴合的垂直面的垂直度（mm） 在100行程上 | 0.016 | 0.02 | 0.02 | ＞0.02 | |||
5、工件头部对工件杆部中心线的偏移量（mm） | ＜0.20 | 0.20~0.25 | 0.25~0.30 | ＞0.30 | |||
（二）生产率（件/分） | |||||||
20mm | ＞80 | 70 | 65 | ＜65 | |||
30mm | ＞60 | 50 | 45 | ＜45 | |||
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条