1) fracture speed
裂纹扩展的速度
2) crack propagation rate
裂纹扩展速度
1.
The CF crack propagation rate (in platform region) of martensitic GC-4 steel ismuch higher than that of bainitic one.
5%NaCl溶液中的CF裂纹扩展曲线上,都出现了类似于应力腐蚀的平台区,而且马氏体组织GC-4钢的平台区裂纹扩展速度远大于贝氏体组织。
2.
As the isothermal temperature was changed from 190℃ to 300℃, the SCC crack propagation rate (da/dt)_Ⅱ decreased by one order of magnitude.
5％NaCl溶液中,其应力强度因子门槛值K_(ISCC)没有显著差别,但其应力腐蚀裂纹扩展速度相关较大,随等温温度的升高,应力腐蚀裂纹扩展速度大大降低。
3) crack propagation velocity
裂纹扩展速度
1.
according to the theories of dynamic mechanics and fracture mechanics,we work out the rational impact split thickness by fracture criterion and the studing of crack propagation velocity.
根据动力学及断裂力学的有关理论,对煤体断裂准则及裂纹扩展速度进行了研究,确定了合理的冲劈厚
2.
The fastest crack propagation velocity for Mg-3.
结果表明:在高速冲击条件下,单相Mg-L i合金的裂纹扩展主要是减速过程,且随L i含量增加,由于合金组织结构的转变(hcp→bcc),加之合金中A l的添加而沉淀的MgL i2A l与A lL i粒子的作用,致使Mg-L i合金的裂纹扩展速度显著降低。
3.
The dynamic fracture toughness, crack propagation velocity and arrest toughness of materials were simultaneously obtained with this method.
本文利用Hopkinson单压杆实验装置 ,对材料的弹塑性动态断裂特性进行了研究 ,建立了应力波载荷作用下动态裂纹起裂、扩展、止裂全过程的动态分析方法 ,采用该方法可同时测得材料的动态断裂韧性、裂纹扩展速度和止裂韧性。
4) fracture speed
裂缝扩展速度，裂纹扩展速度
5) dynamic crack propagation speed
动态裂纹扩展速度
6) crack propagation rate of thermal fatigue
热疲劳裂纹扩展速度
补充资料：裂纹
分子式：
CAS号：
性质：材料在应力或环境(或两者同时)作用下产生的裂隙。分微观裂纹和宏观裂纹。裂纹形成的过程称为裂纹形核。已经形成的微观裂纹和宏观裂纹在应力或环境(或两者同时)作用下，不断长大的过程，称为裂纹扩展或裂纹增长。裂纹扩展到一定程度，即造成材料的断裂。裂纹可分为：交变载荷下的疲劳裂纹；应力和温度联合作用下的蠕变裂纹；惰性介质中加载过程产生的裂纹；应力和化学介质联合作用下的应力腐蚀裂纹；氢进入后引起的氢致裂纹。每一类裂纹的形成过程及机理都不尽相同。裂纹的出现和扩展，使材料的机械性能明显变差。抗裂纹性是材料抵抗裂纹产生及扩展的能力，是材料的重要性能指标之一。
CAS号：
性质：材料在应力或环境(或两者同时)作用下产生的裂隙。分微观裂纹和宏观裂纹。裂纹形成的过程称为裂纹形核。已经形成的微观裂纹和宏观裂纹在应力或环境(或两者同时)作用下，不断长大的过程，称为裂纹扩展或裂纹增长。裂纹扩展到一定程度，即造成材料的断裂。裂纹可分为：交变载荷下的疲劳裂纹；应力和温度联合作用下的蠕变裂纹；惰性介质中加载过程产生的裂纹；应力和化学介质联合作用下的应力腐蚀裂纹；氢进入后引起的氢致裂纹。每一类裂纹的形成过程及机理都不尽相同。裂纹的出现和扩展，使材料的机械性能明显变差。抗裂纹性是材料抵抗裂纹产生及扩展的能力，是材料的重要性能指标之一。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。