1) iron sulfide blackening
硫化铁黑变
2) sulfide black
硫化黑变
1.
This article analyzed the principle of sulfide black formed inside of can of pork lunchern meat, and described how to prevent the metal reaction between the product and inside wall of can.
分析了午餐肉罐头硫化黑变的机理 ,围绕如何防止内容物与罐头内壁金属的反应 ,采用马口铁表面含铬量、镀锡量和涂料三因素三水平进行正交试验 ,样品经装罐、杀菌、保温2～ 180d后开罐评价硫化斑及硫化铁生成情况 ,通过正交试验数据分析 ,探讨对午餐肉罐头容器材料的选
3) black pyrite ore
硫铁矿黑矿
4) sulfur black
硫化黑，棉黑
5) sulfur black
硫化黑
1.
Study on preparatin of sodium thiosulfate by sulfur black wastewater
用硫化黑废水制取硫代硫酸钠的研究
2.
The dose of sulfur black and disperse black,the dyeing sequence of cotton and polyester,and whether the pretreatment will affect the dye depth and fastness of the polyester/cotton fabric were discussed.
本文研究了固体硫化黑染料对涤/棉织物的染色工艺,讨论了硫化黑染料和分散黑染料用量、染棉和染涤的先后顺序、是否经过前处理等工艺对涤/棉织物染色深度和染色牢度的影响,结果证明,使用两浴法用硫化黑染涤/棉的染色效果很好,并且可省去前处理工艺。
3.
The precision and accuracy of the method was good and the method was applied to determination of chloride ion in extraction of the thiosulfate sodium from the wastewater in the process of the Sulfur Black dyes.
该方法精密度及准确度均较好,并已应用于硫化黑工艺废液提取硫代硫酸钠过程中Cl-的检测。
6) C.I.Sulphur Black 1(53185)
硫化黑 BRN
补充资料：硫化铁
铁和硫的化合物的通称，主要有二硫化铁、硫化亚铁和三硫化二铁。
二硫化铁 FeS2为黄色晶体，是黄铁矿的主要成分，有反磁性。黄铁矿的熔点为1171℃，密度5.0克／厘米3，具有立方晶格；室温时为非活性物质，温度升高后变活泼，在空气中加热，氧化成三氧化二铁（见氧化铁）和二氧化硫；在真空中加热到 600℃以上得到硫。二硫化铁可用于硫酸工业。
硫化亚铁 FeS为棕黑色块状物;熔点1193～1199℃，密度4.74克／厘米3；不溶于水，溶于酸的水溶液,同时产生硫化氢；在空气中加热容易氧化，在真空中加热到1100℃以上得到硫。硫化亚铁可由两个元素直接反应制得，也可由亚铁盐水溶液与碱金属硫化物作用而得。在实验室中它可用来发生硫化氢气体；还可用于陶瓷和油漆颜料工业。
三硫化二铁 Fe2S3为黄绿色固体;相对密度4.3;强热则分解；不溶于水,在热水中分解成硫化亚铁和硫;遇酸分解，放出硫化氢气体。
二硫化铁 FeS2为黄色晶体，是黄铁矿的主要成分，有反磁性。黄铁矿的熔点为1171℃，密度5.0克／厘米3，具有立方晶格；室温时为非活性物质，温度升高后变活泼，在空气中加热，氧化成三氧化二铁（见氧化铁）和二氧化硫；在真空中加热到 600℃以上得到硫。二硫化铁可用于硫酸工业。
硫化亚铁 FeS为棕黑色块状物;熔点1193～1199℃，密度4.74克／厘米3；不溶于水，溶于酸的水溶液,同时产生硫化氢；在空气中加热容易氧化，在真空中加热到1100℃以上得到硫。硫化亚铁可由两个元素直接反应制得，也可由亚铁盐水溶液与碱金属硫化物作用而得。在实验室中它可用来发生硫化氢气体；还可用于陶瓷和油漆颜料工业。
三硫化二铁 Fe2S3为黄绿色固体;相对密度4.3;强热则分解；不溶于水,在热水中分解成硫化亚铁和硫;遇酸分解，放出硫化氢气体。