1) eutectic deformation
共晶变形
3) eutectic transformation
共晶转变
1.
Solidifying structures and eutectic transformation form of alumina/zinc alloy composites;
氧化铝/锌合金复合材料的凝固组织及其共晶转变模式
4) eutectic modification
共晶变质
5) conformal deformation
共形形变
1.
This paper deals with the conformal deformation of the smooth Riemannian manifold(Mn,g)(n≥2).
本文考查光滑黎曼流形 ( Mn ,g) ( n≥ 2 )的共形形变 。
6) Deformation Twin
形变孪晶
1.
The results show that, most annealing twin microstruc- ture distribute in austenite matrix of annealed sample, and the deformation twin formed during tensile strain make the sample attain high strength and high plasticity.
结果表明,轧制后退火处理钢板的室温组织为奥氏体基体中存在大量的退火孪晶,在拉伸变形中形成的形变孪晶使产品获得了高强度、高塑性。
2.
Microstructure characteristics of adiabatic shear deformation and deformation twins on both sides of QBe2 and T2 were investigated by means of optical microscope and SEM electronic backscatter diffraction techniques.
结果表明:由于T2和QBe2在物理性能、力学性能和热学性能上的差异,在爆炸载荷条件下只在QBe2中产生绝热剪切带,并且绝热剪切带内分布有十分细小的等轴晶;带内晶粒取向基本相同,带与带之间基体中的晶粒取向也基本相同,且两者还存在较大的取向差;爆炸冲击加载后,QBe2和T2两侧均产生了形变孪晶。
3.
A new type of intersection mechanism of deformation twins with α2 plates in γ TiAl based alloy deformed at room temperature was 
利用透射电镜在室温变形的γ-TiAl基合金中研究了一种新的形变孪晶与α2片的交截机制。
补充资料：共晶
共晶
eutectic
共晶eutectic一定成分的合金液体冷却时，转变为两种或更多紧密混合的固体的恒温可逆反应。这种反应形成的组织即为共晶组织。最简单的共晶反应是在二元合金系统中，具有共晶成分的液体L，在共晶温度下同时凝固形成两固体相a和刀共晶组织。通常用公式L禅a+刀表示。在此共晶反应温度下，出现L、a及刀三相共存。以此方式凝固的合金为共晶合金。偏离共晶成分的合金组织为亚共晶或过共晶。在冷却过程中，这些合金首先从液体中析出树枝状的先共晶组织，然后在枝晶间的液体凝固成共晶组织。可通过高的冷却速度或在液固界面高的温度梯度来抑制先共晶组织的形成，使液体可以直接通过共晶方式凝固;并可调节a及刀相的体积分量与液体的成分相适应。通常这种共晶组织又称为伪共晶。 共晶合金由于熔点低，熔化工艺相对比较简单，并且成本亦低。由于凝固的温度范围很小，改善了铸造流动性，并可抑制热缩孔、疏松及成分偏析。共晶合金具有细而分隔的多相显微组织，可以认为是具有各种特殊性能的复合材料。根据此原理，已开发出镍基和钻基共晶合金，用作抗蟠变材料，可制作喷气发动机叶片。 (汪复兴)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。