1) pitting initiation potential
点蚀发生电位
2) Pitting corrosion potential
点蚀电位
1.
Some comparing analysis on the surface passivated hemostatic forceps domestic and foreign made were carried out through chemical composition analysis,hardness test,microstructure observation and pitting corrosion potential test.
对国内外同一类表面钝化止血钳进行了化学成分、硬度、金相组织和钝化膜点蚀电位等分析。
3) pitting potential
点蚀电位
1.
Effect of test-surface′s selection on measuring pitting potential of carbon steel;
试验面选取对碳钢点蚀电位测量的影响
2.
The effects of temperature,pH,Cl~-and SO~(2-)_4 concentration on pitting potential of 321 stainless steel were investigated by using quadrature test design and contrastive test.
通过正交设计和对比实验研究了温度、pH值以及Cl-和SO42-含量对321不锈钢点蚀电位的影响。
3.
The effects of main test parameters on the process of pitting potential of carbon steels have been studied by quasi-steady-state polarization technique and metallographical analysis technique.
采用准稳态的极化试验研究了各主要试验参数对碳钢在3%NaCl溶液中点蚀电位的影响,结果表明:3种碳钢钝化的临界pH值约为8 0 ;当T =2 0℃～35℃时,点蚀电位值Eb10 0 随温度的降低而变正;当电位变化速度慢于30mV/ 30s时,Eb10 0 随电位变化速度的减小而变负;试验面的粗糙度越大,点蚀电位越
4) re-passivation potential
点蚀保护电位
5) critical pitting potential
临界点蚀电位
补充资料：点蚀
分子式：
CAS号：
性质：又称坑蚀，斑点腐蚀，小孔腐蚀或点蚀。金属表面大部分区域腐蚀相对较轻，而某些局部出现向纵深发展的腐蚀小孔的腐蚀形态。孔蚀的原因是活性阴离子导致表面钝化膜局部破坏。具有钝化能力的金属如不锈钢、铝合金及碳钢等，在含氯离子介质中经常发生孔蚀。蚀孔的发展速度有时很快，可以深入金属甚至短时间内蚀穿金属截面，且较难预测，因此孔蚀往往比均匀腐蚀具有更大的危害性。可以通过降低介质中的有害阴离子浓度，采用涂层保护、添加缓蚀剂和阴极保护等方法予以减轻或防止。
CAS号：
性质：又称坑蚀，斑点腐蚀，小孔腐蚀或点蚀。金属表面大部分区域腐蚀相对较轻，而某些局部出现向纵深发展的腐蚀小孔的腐蚀形态。孔蚀的原因是活性阴离子导致表面钝化膜局部破坏。具有钝化能力的金属如不锈钢、铝合金及碳钢等，在含氯离子介质中经常发生孔蚀。蚀孔的发展速度有时很快，可以深入金属甚至短时间内蚀穿金属截面，且较难预测，因此孔蚀往往比均匀腐蚀具有更大的危害性。可以通过降低介质中的有害阴离子浓度，采用涂层保护、添加缓蚀剂和阴极保护等方法予以减轻或防止。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。