1) copper-nickel-antimony-lead bronze
铜镍锑铅合金
2) nickel-antimony-lead bronze
镍锑铅青铜
3) Pb-Sb alloy
铅锑合金
1.
The kinetics of antimony leaching from oxidizing-converting slag of Pb-Sb alloy by HCl-NaCl was approached using the shrinking unreacted core model for the reaction of liquid?solid.
用液-固多相反应的收缩未反应核模型研究了在HCl-NaCl浸出铅锑合金氧化吹炼渣过程中锑的浸出动力学。
4) Lead-Antimony alloy
铅锑合金
1.
The new technology of directly producing Antimony Oxide from Lead-Antimony alloy is discussed in the paper.
介绍了利用铅锑合金直接生产氧化锑的技术,并与火法除铅剂除铅分离技术进行了比较,采用该种工艺可获得较好的技术经济指标,并提高了锑资源的综合利用率。
2.
The advantage and drawback of lead-antimony alloy used as grids material and the work principle of lead-acid battery were in detail introduced.
详细介绍了铅锑合金用作为板栅材料的优越性及存在的问题和铅蓄电池的工作原理,探讨了锑在充放电过程中的微观作用机理,提出了解决铅锑合金用作为板栅材料早期容量损失(PCL)及失水严重的几种途径及实施的可能性,以提高铅锑合金在铅蓄电池板栅材料的应用性能。
3.
Based on the experience and data from manufacturing lead-calcium alloy and lead-antimony alloy for several years,this paper firstly presented the idea and theoretical model of "relatively fluctuating range " for controlling the composition oflead-based alloy.
在多年生产铅锑合金与铅钙合金的基础上,首次提出了配制铅基合金“相对波动范围”的相关概念及理论模型,探讨了铅基合金相对波动范围值与成分的关系,为提高配制铅锑合金与铅钙合金的一次合格率指明了有效途径。
5) lead antimony alloy
铅锑合金
1.
Effect of titanium ion implantation on corrosion behaviors of lead and lead antimony alloy (II);
钛离子注入对铅和铅锑合金腐蚀行为影响的研究(Ⅱ)
2.
A method for the determination of As, Bi, Ca, Cd, Co, Fe, Mn, Se and Zn in lead antimony alloy by ICP AES was proposed.
拟定了电感耦合等离子体原子发射光谱 (ICP -AES)测定铅锑合金中As、Bi、Ca、Cd、Co、Fe、Mn、Se和Zn等九个元素的分析方法 ,考察了Pb、Sb基体对待测元素的干扰情况。
3.
The anodic films on lead and lead antimony alloys formed in sulfuric acid solution at potentiostatic polarization were investigated by means of the XPS and AES methods.
３５Ｖ恒电位极化形成的铅和铅锑合金阳极膜，发现锑对阳极膜表面层二氧化铅的生长有明显抑制作用；利用ＡＥＳ结合Ａｒ＋刻蚀技术对其内层主要组成元素作深度分布分析，发现锑能够显著提高阳极膜内部二氧化铅的含量，从而使铅锑合金阳极膜较之纯铅阳极膜具有更为优越的导电性。
6) Pb-Sb alloys
铅锑合金
1.
In this paper,the analysis way of lead in raw lead and Pb-Sb alloys was studied.
研究了粗铅及铅锑合金中铅的测定方法。
补充资料：铅锑合金
分子式：
CAS号：
性质：制造铅酸蓄电池板栅和导电零件的一种含锑的铅基合金。与纯铅相比，熔点较低，熔融状态下流动性好，易于浇铸成型，凝固后硬度大；缺点是板栅的气体析出超电势低。为了减少蓄电池的充电时气体的析出，减少自放电并提高耐腐蚀性，含锑量已由传统的5%～7%逐步降低至2%左右甚至更低。同时也有选择地加入了少量的其他成分如锡、砷、硫、硒和铜等以改善合金的物理和化学性能。
CAS号：
性质：制造铅酸蓄电池板栅和导电零件的一种含锑的铅基合金。与纯铅相比，熔点较低，熔融状态下流动性好，易于浇铸成型，凝固后硬度大；缺点是板栅的气体析出超电势低。为了减少蓄电池的充电时气体的析出，减少自放电并提高耐腐蚀性，含锑量已由传统的5%～7%逐步降低至2%左右甚至更低。同时也有选择地加入了少量的其他成分如锡、砷、硫、硒和铜等以改善合金的物理和化学性能。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条