1.
Samples were then taken for examination on chemical analysis,microstructure,micro hardness,micro-fracture on those spalled work rolls.
通过对某厂1700冷连轧机工作辊剥落事故进行调查和断口特征分析,发现该轧机工作辊出现由工作辊内部线状开裂引起的剥落;对剥落工作辊进行取样检验,分析其化学成分、金相组织、显微硬度、残余奥氏体含量和微观断口,证实工作辊辊身表层基体组织不符合技术要求、显微硬度和残余奥氏体含量过高是导致工作辊内裂剥落的主要原因,进而实施改进措施,防止事故再次发生。
5) macrofractography
['mækrəfræk'tɔɡrəfi]
宏观断口
1.
According to test chemical composition,macrofractography and observation of microstructure to a failure workpiece,the results show that there are much Widmanstatten structure and more MnS inclusions in the failure workpiece,and lead to failure of swing in the rolling direction.
借助于扫描电镜、光学显微镜对汽车上摆臂HP295热轧板材断裂原因进行失效分析,通过对汽车摆臂化学成分的测定、宏观断口及显微组织的观察,确定工件内部存在严重的质量问题。
2.
According to test chemical composition, macrofractography and observation of microstructure of failure piston,finding some important questions in the workpiece.
借助于扫描电镜、光学显微镜对内燃机铸造铝活塞顶部破裂原因进行了失效分析,通过对失效铝活塞化学成分的测定、宏观断口及显微组织的观察,确定工件内部存在严重的质量问题。
3.
According to test chemical composition,macrofractography and observation of microstructure to a failure workpiece,the results show that there are much Widmanstatten structure and more MnS inclusions in the failure workpiece,and lead to failure of swing in the rolling direction.
借助于扫描电镜、光学显微镜对汽车上摆臂 HP295热轧板材断裂原因进行失效分析,通过对汽车摆臂化学成分的测定、宏观断口及显微组织的观察,确定工件内部存在严重的质量问题。
6) flashover on circuit breaker chamber
断口外闪
补充资料:断口
分子式:
分子量:
CAS号:
性质:矿物晶体受打击后所产生的无一定方向的破裂面。根据破裂面的形态,可分为贝壳状、平坦状、锯齿状、参差状等。例如石英的断口的是贝壳状。
分子量:
CAS号:
性质:矿物晶体受打击后所产生的无一定方向的破裂面。根据破裂面的形态,可分为贝壳状、平坦状、锯齿状、参差状等。例如石英的断口的是贝壳状。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条