1) graphite ignition anode
石墨引燃阳极
2) graphite anode
石墨阳极
1.
On the analysis of the oxidation mechanism of graphite anode in calcium molten salt electrolysis process, the resist-oxidation of the graphite anode is investigated.
在对钙熔盐电解过程中石墨阳极氧化机制分析的基础上,进行石墨阳极抗氧化研究。
2.
The consumption of the graphite anode in the calcium molten salt electrolysis process is analyzed, which includes oxidation consumption and physics damage.
分析了钙熔盐电解过程石墨阳极消耗的两个因素 ,即主要有氧化消耗和物理破损 。
3) natural graphite anode
天然石墨阳极
1.
A new approach was proposed to modify the surface structure of natural graphite by use of polymer adsorption and thereby to improve the initial charge-discharge efficiency of natural graphite anode in Li-ion battery.
针对天然石墨阳极存在的首次充放电效率低这一应用问题,提出了采用聚合物表面修饰石墨的新方法。
4) graphite anode electrolytic cell
石墨阳极电解槽
5) artificial graphite anode
人造石墨阳极
6) graphitised anode block
石墨化阳极块
补充资料：石墨阳极
分子式：
CAS号：
性质：用于电解食盐水溶液电解槽的阴极。这种石墨均用人造石墨，具有适当密度（2.21g/cm3）、孔隙率小（<27%）、抗压强度和抗折强度高（分别为24.5～29.4MPa和18.2～21.57MPa）等特点。电石油焦、沥青焦、无烟煤、沥青等压制成型并在近3000℃的高温下石墨化而成，通常还经半干性油、有机溶剂或树脂如亚麻仁油、桐油、石蜡、四氯化碳等进行二次浸渍（全浸法，根部浸渍法），以增加其密度，降低孔隙率。用于隔膜电解和水银电解法生产烧碱中。
CAS号：
性质：用于电解食盐水溶液电解槽的阴极。这种石墨均用人造石墨，具有适当密度（2.21g/cm3）、孔隙率小（<27%）、抗压强度和抗折强度高（分别为24.5～29.4MPa和18.2～21.57MPa）等特点。电石油焦、沥青焦、无烟煤、沥青等压制成型并在近3000℃的高温下石墨化而成，通常还经半干性油、有机溶剂或树脂如亚麻仁油、桐油、石蜡、四氯化碳等进行二次浸渍（全浸法，根部浸渍法），以增加其密度，降低孔隙率。用于隔膜电解和水银电解法生产烧碱中。