1) corrosion microbiology
腐蚀微生物学
2) MIC
[英][maɪk] [美][maɪk]
微生物腐蚀
1.
SENSITIVITIES OF MAGNESIUM ALLOY AND OTHERMETALS TO MICROBIOLOGICALLY INFLUENCED CORROSION;
镁合金与其它金属的微生物腐蚀行为比较
2.
Corrosion Mechanism of MIC and Influences on Corrosion and Protection of Underground Pipeline;
微生物腐蚀机理及对埋地管道腐蚀防护的影响
3.
THE ROLE OF Ca~(2+) ON THE MICROBIOLOGICALLY INDUCED CORROSION OF CARBON STEEL;
钙离子对碳钢微生物腐蚀的影响
3) microbiologically influenced corrosion
微生物腐蚀
1.
Development of microbiologically influenced corrosion(MIC) and corrosion inhibition using microorganisms in the seawater circulating cooling system;
海水循环冷却水的微生物腐蚀和生物防腐研究进展
2.
A Comparative Study of Microbiologically Influenced Corrosion of Two Kinds of Copper Alloy;
两种铜合金微生物腐蚀的比较研究
3.
Role of the biofilm in the microbiologically influenced corrosion of Cu-30Ni alloy was studied based on a comparative study on samples immersed in environments with and without SRB.
采用电化学阻抗谱、扫描电镜和X射线能谱分析等技术研究了硫酸盐还原菌(SRB)作用下B30合金表面生物膜的结构及其对合金微生物腐蚀的影响。
4) Microbiological corrosion
微生物腐蚀
1.
Microbiological Corrosion and Protection of Magnesium Alloys of lubricate System of Aero-engine;
航空发动机滑油系统镁合金微生物腐蚀与防护
2.
The causes of high corrosion rate in the circulationg cooling water system of chemical fertilizer plant were analyzed from electrochemical corrosion, microbiological corrosion and detrimental ions corrosion.
从电化学腐蚀、微生物腐蚀、有害离子腐蚀等三个方面 ,对大化肥循环水系统腐蚀率高的原因进行了分析 ,认为其主要原因是氨介质泄漏引起的微生物腐蚀 ;同时 ,提出了具体的处理措
3.
Thiobacillus denitrificans(TDN) was used to control the microbiological corrosion of carbon steel caused by Sulfate-reducing bacteria(SRB).
将脱氮硫杆菌(TDN)作用于被硫酸盐还原菌(SRB)微生物腐蚀的碳钢,研究了SRB和TDN生长特性及最适生长条件。
5) Microbiologically influenced corrosion (MIC)
微生物腐蚀
1.
With increasingly intensive exploitation and effective utilization of marine resources, problems due to microbiologically influenced corrosion (MIC) of metal constructions/components had aroused people’s high concern and extensive study, and among them sulfate-reducing bacteria (SRB) are of the most dangerous culprits.
随着人们对海洋资源的深入开发和有效利用,海洋环境中金属结构建筑物的微生物腐蚀(microbiologically influenced corrosion, MIC)已引起了人们的高度重视和广泛研究。
6) microbial corrosion
微生物腐蚀
1.
The composition of sewage and its metabolite produced by microorganism are briefly described at first,and then the present status and progress of mechanism study of microbial corrosion of concrete are introduced.
简要叙述了污水组成及其微生物代谢产物,介绍了混凝土微生物腐蚀的作用机制及其研究现状,并论述了当前关于混凝土微生物腐蚀研究的主要内容、采取的腐蚀实验方案和相关的微生物学方法,最后强调了国内开展混凝土微生物腐蚀研究的紧迫性。
2.
s:Related bacterial types of microbe are screened based on destroyed situation resulted from microbial corrosion of underwater metallic and concrete structure of water power and hydroelectric engineering.
根据水利水电工程水下金属结构和混凝土结构受到微生物腐蚀破坏的状况,筛选出相关微生物的菌种,确定接触型抗微生物腐蚀涂料用树脂、交联剂和杀菌剂的种类及用量。
3.
Damage of microbial corrosion of concrete was presented,then the corrosion mechanism was introduced,and the measures and problems in microbial corrosion of concrete were described,finally the future development was prospected.
介绍了混凝土微生物腐蚀的危害,结合混凝土微生物腐蚀的作用机理,分析了国内外混凝土微生物腐蚀防治措施的研究现状和存在的问题,并展望了未来的发展趋势。
补充资料：腐蚀微生物
参与或促进金属腐蚀过程的微生物。1910年，R.H.盖恩斯发现微生物腐蚀。1934年,荷兰学者C.A.H.vonW.屈尔等提出硫酸盐还原菌参与金属腐蚀中阴极氢去极化的理论之后，人们对微生物腐蚀开始重视起来。
腐蚀微生物主要是在自然界中参与硫、铁元素循环的菌类，包括好氧菌和厌氧菌。好氧菌有硫杆菌属，如氧化硫杆菌、氧化亚铁硫杆菌和排硫硫杆菌等。它们分布于含硫的酸性矿水、土壤及海洋淤泥中，通过氧化元素硫和还原性硫化物，最终产生硫酸而腐蚀金属、混凝土构件等。铁细菌能氧化水中亚铁成高铁氧化物沉积于菌体外鞘或周围粘液层中，在金属表面形成黄褐色的结瘤。结瘤内氧进入困难而导致氧浓差电池腐蚀。常见的危害菌有嘉利翁氏菌属、纤发菌属、泉发菌属和鞘铁菌属等。此外，一些产生粘液的细菌（如假单孢菌属中的细菌）、真菌以及某些藻类和原生动物，都可引起金属腐蚀。厌氧菌主要是硫酸盐还原菌，广泛分布于pH6～9的土壤、淡水、海水、淤泥中。在金属腐蚀中出现最多的是脱硫弧菌，它将自然界中存在的硫酸盐还原成硫化物。微生物腐蚀常给地下管线、海底电缆、工业注?低车裙ひ瞪枋┐囱现匚：Γ斐删蒙系乃鹗А?
通常是在土壤和水介质中采用耐菌破坏的有机护层（煤焦油沥青、环氧树脂漆、塑料薄膜等）或无机护层（镀锌、铬、水泥等）以及阴极保护（包括牺牲阳极或外加电源法）等措施，以防止微生物腐蚀。在密闭系统中（如金属油、气贮罐、飞机油箱、工业循环冷却装置等），采用氧化型或非氧化型杀菌剂杀灭或抑制腐蚀微生物的增殖，达到控制腐蚀的目的。
腐蚀微生物主要是在自然界中参与硫、铁元素循环的菌类，包括好氧菌和厌氧菌。好氧菌有硫杆菌属，如氧化硫杆菌、氧化亚铁硫杆菌和排硫硫杆菌等。它们分布于含硫的酸性矿水、土壤及海洋淤泥中，通过氧化元素硫和还原性硫化物，最终产生硫酸而腐蚀金属、混凝土构件等。铁细菌能氧化水中亚铁成高铁氧化物沉积于菌体外鞘或周围粘液层中，在金属表面形成黄褐色的结瘤。结瘤内氧进入困难而导致氧浓差电池腐蚀。常见的危害菌有嘉利翁氏菌属、纤发菌属、泉发菌属和鞘铁菌属等。此外，一些产生粘液的细菌（如假单孢菌属中的细菌）、真菌以及某些藻类和原生动物，都可引起金属腐蚀。厌氧菌主要是硫酸盐还原菌，广泛分布于pH6～9的土壤、淡水、海水、淤泥中。在金属腐蚀中出现最多的是脱硫弧菌，它将自然界中存在的硫酸盐还原成硫化物。微生物腐蚀常给地下管线、海底电缆、工业注?低车裙ひ瞪枋┐囱现匚：Γ斐删蒙系乃鹗А?
通常是在土壤和水介质中采用耐菌破坏的有机护层（煤焦油沥青、环氧树脂漆、塑料薄膜等）或无机护层（镀锌、铬、水泥等）以及阴极保护（包括牺牲阳极或外加电源法）等措施，以防止微生物腐蚀。在密闭系统中（如金属油、气贮罐、飞机油箱、工业循环冷却装置等），采用氧化型或非氧化型杀菌剂杀灭或抑制腐蚀微生物的增殖，达到控制腐蚀的目的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。