1) nitrocellulose finish
硝纤涂饰剂
2) nitrocellulose binder
硝化纤维涂饰剂
3) cellulose pigment finish
有色硝纤涂饰剂
4) nitrocellulose finish
硝化纤维素涂饰剂;硝纤涂饰剂
5) spray finish
喷涂涂饰剂
6) finishing agent
涂饰剂
1.
The preparation methods of acrylic modified aqueous polyurethane dispersion as leather finishing agent were reviewed, including co-mixture crosslinking, copolymerization emulsion, seed emulsion polymerization and interpenetrating polymer network polymerization.
综述了近年来丙烯酸酯改性水性聚氨酯(PUA)皮革涂饰剂的改性方法,包括共混交联法、溶液聚合法、种子乳液聚合法和互穿网络聚合法。
2.
A kind of aqueous polyurethane finishing agents were synthesized with isophorone diisocyanate(IPDI),polytetrahydrofuran(PTMG),dimethylolpropanoic acid(DMPA) as monomers and n-butylamine,ethylene glycol and ethylenediamine as chain-extension agents.
采用异佛尔酮二异氰酸酯(IPDI)、二羟甲基丙酸(DMPA)、聚四氢呋喃(PTMG)为原料制备聚氨酯预聚体,分别以乙二醇(EG)、乙二胺(EN)和正丁胺(n-butylamine)为扩链剂制备了水性聚氨酯皮革涂饰剂,研究了该涂饰剂所成膜的力学性能、断裂伸长率和吸水性。
3.
Collagen hydrolysate was used to modify the polyurethane finishing agent in different reaction stages.
经过该涂饰剂涂饰的皮革的透湿率较高,可达689mg/10cm2·24h。
补充资料：硝化纤维涂饰剂
分子式：
CAS号：
性质：又称硝化纤维涂饰剂。皮革涂饰用成膜剂，成膜快、光亮度高，耐水、耐干湿摩擦，可不用甲醛固定，涂层不发黏、手感舒适。但不耐老化，膜易变硬而脆、变黄，透气性和延伸性差。有溶剂型、乳液型和水油两用型等品种。溶剂型硝酸纤维成膜剂、光亮很好，但有毒，对大气污染。现代多用硝酸纤维乳液做顶层涂饰的光亮剂。为了改正硝酸纤维成膜剂的缺点，可用聚氨酯或丙烯酸树脂、醇酸树脂以及有机硅等改性。硝酸纤维乳液制备方法：将硝酸纤维(含氮量为11.7%～12.3%，黏度1/2s)溶于有机溶剂中，再与增塑剂混合均匀，配制成油相。将乳化剂、渗透剂和去离子水混合均匀，配制成水相。然后将水相缓慢滴加入油相中并高速搅拌，加完料后继续搅拌1h，最后用超声波振荡器粉碎10min即成。
CAS号：
性质：又称硝化纤维涂饰剂。皮革涂饰用成膜剂，成膜快、光亮度高，耐水、耐干湿摩擦，可不用甲醛固定，涂层不发黏、手感舒适。但不耐老化，膜易变硬而脆、变黄，透气性和延伸性差。有溶剂型、乳液型和水油两用型等品种。溶剂型硝酸纤维成膜剂、光亮很好，但有毒，对大气污染。现代多用硝酸纤维乳液做顶层涂饰的光亮剂。为了改正硝酸纤维成膜剂的缺点，可用聚氨酯或丙烯酸树脂、醇酸树脂以及有机硅等改性。硝酸纤维乳液制备方法：将硝酸纤维(含氮量为11.7%～12.3%，黏度1/2s)溶于有机溶剂中，再与增塑剂混合均匀，配制成油相。将乳化剂、渗透剂和去离子水混合均匀，配制成水相。然后将水相缓慢滴加入油相中并高速搅拌，加完料后继续搅拌1h，最后用超声波振荡器粉碎10min即成。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。