2) Cr12 type stainless steel
Cr12型不锈钢
1.
Cracks occured frequently on the surface of certain parts made of Cr12 type stainless steels.
某些Cr12型不锈钢零件时常出现表面裂纹,通过了解这些零件的生产过程、裂纹形态及其扩展方式等,采用模拟试验分析了裂纹的形成机制,在此基础上建立了分析Cr12型马氏体不锈钢零件淬裂原因的基本流程。
3) stainless section steel
不锈钢型材
1.
Simulation of stretch bending forming process of stainless section steel;
不锈钢型材拉弯成形工艺模拟研究
5) Modified Type 202 Steel
改进型202不锈钢
6) modified 316L stainless steel
改进型316L不锈钢
1.
Dependence of radiation damage in the modified 316L stainless steel has been investigated on irradiation temperature from room temperature to 802 ℃ at 21 and 33 dpa and on irradiation dose up to 100 displacemets/atom(dpa) at room temperature by the heavy ion irradiation simulation and positron annihilation lifetime techniques.
用重离子辐照模拟和正电子湮没寿命技术研究了改进型316L不锈钢在21和33 dpa辐照剂量下的辐照损伤在室温到802℃温度范围随辐照温度变化和室温下0-100 dpa剂量范围随辐照剂量变化。
补充资料：不锈钢知识（系列12）
316和316L不锈钢
316和317不锈钢（317不锈钢的性能见后）是含钼不锈钢种。317不锈钢中的钼含量略高明于316不锈钢.由于钢中钼，该钢种总的性能优于310和304不锈钢，高温条件下，当硫酸的浓度低于15％和高于85％时，316不锈钢具有广泛的用途。316不锈钢还具有良好的而氯化物侵蚀的性能，所以通常用于海洋环境。
316和317不锈钢（317不锈钢的性能见后）是含钼不锈钢种。317不锈钢中的钼含量略高明于316不锈钢.由于钢中钼，该钢种总的性能优于310和304不锈钢，高温条件下，当硫酸的浓度低于15％和高于85％时，316不锈钢具有广泛的用途。316不锈钢还具有良好的而氯化物侵蚀的性能，所以通常用于海洋环境。
316L不锈钢的最大碳含量0.03,可用于焊接后不能进行退火和需要最大耐腐蚀性的用途中。
耐腐蚀性：耐腐蚀性能优于304不锈钢，在浆和造纸的生产过程中具有良好的耐腐蚀的性能。而且316不锈钢还耐海洋和侵蚀性工业大气的侵蚀。
耐热性：在1600度以下的间断使用和在1700度以下的连续使用中，316不锈钢具有好的耐氧化性能：在800-1575度的范围内，最好不要连续作用316不锈钢，但在该温度范围以外连续使用316不锈钢时，该不锈钢具有良好的耐热性。316L不锈钢的耐碳化物析出的性能比316不锈钢更好，可用上述温度范围。
热处理：在1850-2050度的温度范围内进行退火，然后迅速退火，然后迅速冷却。316不锈钢不能过热处理进行硬化。
焊接：316不锈钢具有良好的焊接性能。可采用所有标准的焊接方法进行焊接。焊接时可根据用途，分别采用316Cb、316L或309Cb不锈钢填料棒或焊条进行焊接。为获得最佳的耐腐蚀性能，316不锈钢钢的焊接断面需要进行焊后退火处理。如果使用316L不锈钢，不需要进行焊后退火处理。
典型用途：纸浆和造纸用设备热交换器、染色设备、胶片冲洗设备、管道、沿海区域建筑物外部用材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。