1) galvanizing brittlement
镀锌脆性
2) zinc sensitivity of hydrogen attack
镀锌氢脆
1.
The large welding current caused the formation of quenched martensite and the high residual stresses in the welding zone,resulting in the increase of zinc sensitivity of hydrogen attack.
结果表明:由于焊接电流过大,使焊缝产生淬火马氏体组织及较大的焊接残余应力,导致镀锌氢脆敏感性增加,造成吸油盘发生氢脆开裂。
3) embrittlement of electrodeposited coatings
镀层脆性
4) alkaline zinc plating
碱性镀锌
1.
Influencing factors to the uniformity of coating thickness for alkaline zinc plating have been studied systematically by Hall-cell test.
采用霍尔槽试验对碱性镀锌镀层厚度均一性的影响因素进行了研究。
5) acid Zinc plating
酸性镀锌
1.
In this paper, a kind of acid Zinc plating process is introduced.
本文介绍了一种大幅度提高紧固件耐腐蚀性能的氯化钾酸性镀锌工艺,详细叙述了该工艺的配方、配制过程、工艺维护及废水处理。
6) acidic zinc plating
酸性镀锌
1.
A treatment method of iron impurity in an acidic zinc plating bath was studied and the existent problem was analyzed.
试验了用双氧水处理酸性镀锌溶液中铁杂质的方法,实验表明:在pH=4。
2.
A malfunction brought by quality matter of zinc chloride in an acidic zinc plating bath was analyzed.
对一次由氯化锌质量问题引起的酸性镀锌故障进行了分析,实验表明,这批氯化锌原料含有有机杂质,导致镀层无光泽、发花,用活性炭处理镀液排除了这起故障。
补充资料：镀层脆性
分子式：
CAS号：
性质：控制电镀层品质的指标之一。凡使镀层内应力增大的因素，如有机物在镀层中的夹杂及重金属的共沉积，都有引起镀层发脆的倾向。测定镀层脆性的方法有金属杯突试验法和静压挠曲试验法等。前种试验方法是用一个规定钢球或球状冲头，向夹紧于规定压模内的试样均匀施加压力，直至镀层开始产生裂纹为止。压入的深度值作为镀层脆性的指标，深度越大，脆性越小。静压挠曲试验法的原理与金属杯突试验法相似。
CAS号：
性质：控制电镀层品质的指标之一。凡使镀层内应力增大的因素，如有机物在镀层中的夹杂及重金属的共沉积，都有引起镀层发脆的倾向。测定镀层脆性的方法有金属杯突试验法和静压挠曲试验法等。前种试验方法是用一个规定钢球或球状冲头，向夹紧于规定压模内的试样均匀施加压力，直至镀层开始产生裂纹为止。压入的深度值作为镀层脆性的指标，深度越大，脆性越小。静压挠曲试验法的原理与金属杯突试验法相似。