1) Poly(diallyl isophthalate)/PDAIP
聚间苯二甲酸二烯丙酯
2) poly(diallyl phthalate)
聚邻苯二甲酸二烯丙酯
3) polydiallyl phthalate
聚苯二甲酸二烯丙酯
4) DAIP
间苯二甲酸二烯丙基酯
1.
The properties of maleinized polybutadiene modified DAIP was investigated.
研究了顺酐化聚丁二烯(MPB)对间苯二甲酸二烯丙基酯(DAIP)树脂浇铸体冲击性能、耐热性能、介电性能以及耐盐水性能的影响。
2.
A co-cure method of novolac epoxy resin(F-51)and diallyl isophthalate(DAIP) were used to enhance the heat resistance of epoxy resins.
采用共固化的方法,得到酚醛环氧树脂(F-51)和间苯二甲酸二烯丙基酯(DAIP)的共固化树脂。
5) diallyl isophthalate
间苯二甲酸二烯丙酯
1.
The soakage of the three materials system of TDE-85 epoxy resin, diallyl isophthalate(DAIP) and E-51 epoxy resin in vacuum assistant resin transfer molding(VARTM) for high performance radome was studied.
研究了采用真空辅助树脂传递模塑 (VARTM )工艺制造高性能机载雷达罩的TDE - 85环氧树脂、间苯二甲酸二烯丙酯 (DAIP)和E - 5 1环氧树脂三种材料体系的浸润性能。
2.
The heat resistant solventless insulating impregnating varnish, which mainly comprises of diallyl isophthalate (DAIP ) and vinyl ester (VE), was synthesized and tested.
合成了以间苯二甲酸二烯丙酯 (DAIP)为主体、环氧丙烯酸酯 (VE)为改性剂的耐高温无溶剂绝缘浸渍漆 ,用 DTA分析了漆液的反应特性 ,讨论了 DAIP的预聚、VE含量等因素对漆液、浇铸体性能的影响 ,并对漆的常规性能进行了测试。
6) diallyl isophthalate
间苯二甲酸二烯丙基酯
1.
The prepolymerization of diallyl isophthalate and its curing characteristics are investigated in this paper.
本文研究了间苯二甲酸二烯丙基酯(DAIP)的预聚合及树脂的固化性能。
补充资料：聚间苯二甲酸二烯丙酯模塑料
分子式：
CAS号：
性质：以间苯二甲酸二烯丙酯预聚物为基料制得的模塑料。性能基本与聚邻苯二甲酸二烯丙酯模塑料相似，但耐热性更好。热变形温度316℃，长期使用温度260℃；拉伸强度54.88MPa，弯曲强度88.2MPa，压缩强度54.88MPa；成型收缩率0.2％；体积电阻率1.0×1014Ω·cm，介电常数(106Hz)4.1，介质损耗因素0.01。由间苯二甲酸二烯丙酯聚合而成预聚物后，再与有关添加剂混合制得。主要用作电器元件、开关、插座和插头等。
CAS号：
性质：以间苯二甲酸二烯丙酯预聚物为基料制得的模塑料。性能基本与聚邻苯二甲酸二烯丙酯模塑料相似，但耐热性更好。热变形温度316℃，长期使用温度260℃；拉伸强度54.88MPa，弯曲强度88.2MPa，压缩强度54.88MPa；成型收缩率0.2％；体积电阻率1.0×1014Ω·cm，介电常数(106Hz)4.1，介质损耗因素0.01。由间苯二甲酸二烯丙酯聚合而成预聚物后，再与有关添加剂混合制得。主要用作电器元件、开关、插座和插头等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条