1) attapulgate
无水硅酸铝矿石
2) anhydrous aluminium silicate
无水硅酸铝
3) polygarskite
[,pɔli'ɡɑ:skait]
水合硅酸铝镁矿
4) hydralsite
['haidrəlsait]
水硅铝石
5) Hydrous magnesium silicate mineral
含水铝镁硅酸盐矿物
6) gibbsite
['ɡibzait]
三水铝石矿
1.
To study the sweetening process of diasporic bauxite,Al(OH)3 obtained from the direct carbonization of unrefined sintering solution was used as the additive and its performance was compared with that of the conventionally used gibbsite.
分别以烧结法粗液直接进行深度碳分所得到粗氢氧化铝和工业上常用的三水铝石矿作为添加剂,进行了一水硬铝石矿增溶溶出过程的对比研究,主要考察了增溶温度、添加剂添加量和增溶时间等因素对溶出效果的影响,同时对增溶溶出矿浆与常规拜耳法溶出矿浆的沉降性能进行了对比研究。
2.
The results showed that Weipa ore is gibbsite and its leaching efficiency is high when digested at higher than 200 ℃,so applicable to sweetening ore in digestion process,under conditions that the sweetening process is controlled in the range of 195～200 ℃ for 15～20 min and the dosage of Weipa .
结果表明:韦帕矿为三水铝石矿,在200℃以上溶出时,浸出率较高,适宜作为增溶溶出过程的后加矿。
补充资料：无水硅酸铝
分子式：
CAS号：
性质：纯品为无色晶体，由于氧化铝和二氧化硅的比例不恒定，理化指标差别较大。1:1硅酸铝(Al2O3·SiO2)的相对密度3.247，熔点1545℃(分解)；1:3硅酸铝(Al2O3·3SiO2)的相对密度3.156，熔点1920℃。工业晶系白色粉末，粒径1～1.5μm，相对密度2.2～2.63，pH值4.6～6.5，组成多为1：3硅酸铝。吸湿性小，可作为天然橡胶、合成橡胶、合成树脂及涂料的白色颜料或填料，亦是玻璃和陶瓷工业的重要原料。
CAS号：
性质：纯品为无色晶体，由于氧化铝和二氧化硅的比例不恒定，理化指标差别较大。1:1硅酸铝(Al2O3·SiO2)的相对密度3.247，熔点1545℃(分解)；1:3硅酸铝(Al2O3·3SiO2)的相对密度3.156，熔点1920℃。工业晶系白色粉末，粒径1～1.5μm，相对密度2.2～2.63，pH值4.6～6.5，组成多为1：3硅酸铝。吸湿性小，可作为天然橡胶、合成橡胶、合成树脂及涂料的白色颜料或填料，亦是玻璃和陶瓷工业的重要原料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。