1) hiding power chart
遮盖力图
2) hiding power
遮盖力
1.
Nano-CaCO3 can instead of TiO3( the content was 10% ) or Lithopone, but also doesn't reduce the hiding power,and it has good storing stability.
本文介绍了纳米碳酸钙的制备,在乳胶漆中作为填料对涂料性能的影响,能代替10％的钛白粉或立德粉,不降低遮盖力,并且有良好的贮藏稳定性。
2.
By way of experiments, analysis was made of the effects of reduced PVC on gloss, hiding power and scrubbing resistance of latex paint.
本文通过实验,分析讨论了对比颜料体积浓度对乳胶漆光泽、遮盖力、耐洗刷性的影响,在综合考虑对涂料各性能的不同影响基础上,确定了乳胶漆配方设计中对比颜料体积浓度的最佳范围。
3.
The influence factors of application performance, which includes hiding power, durability, dispersivity and so on, for titanium dioxide are discussed.
分析了影响TiO2遮盖力、耐候性、分散性等应用性能的因素,重点阐述了金红石型TiO2表面包覆硅铝氧化物的方法及对这些应用性能的影响,在此基础上对包覆机理进行探讨。
3) covering power
遮盖力
1.
The results showed that when 20% of TiO2 pigment was substituted by nano-BaSO4,the covering power and the whiteness of the products were increased by 43% and 2.
利用光电分光光度计和分光光度测色仪测定了用白色母粒所制薄膜和样板制品的遮盖力和白度,利用图像分析仪定量表征了颜料的分散情况。
4) covering power agent
遮盖力剂
5) cryptometer
[krip'tɔmitə]
遮盖力计
6) ink mileage, mileage
油墨遮盖力
补充资料：遮盖力
分子式：
CAS号：
性质：色漆、油墨等经均匀涂覆后，其涂膜遮盖被涂表面底色的能力。遮盖力是颜料对光线产生散射和吸收的结果。涂料遮盖力是指把色漆均匀涂布在物体表面上，使其底色不再呈现的最小用漆量。用g/m2表示。颜料遮盖率是指颜料和调墨油研磨成色浆，均匀地涂刷于黑白格底材上，使黑白格恰好被遮盖的最小用颜料量。颜料遮盖力的强弱主要决定于下列性能：(1)折射率，折射率愈大，遮盖力愈强；(2)吸收光线能力，吸收光线能力愈大，遮盖力愈强；(3)结晶度，晶形的遮盖力较强，无定形的遮盖力较弱；(4)分散度，分散度愈大，遮盖力愈强。同样重量的涂料产品，在相同的施工条件下，遮盖力高的产品可比遮盖力低的产品能涂装更多的面积。为了克服目测黑白格板遮盖力的不准确性，用反射率仪对遮盖力进行测定，把被测试样以不同厚度涂布于透明聚酯膜上，干燥后置于黑、白玻璃板上，分别测定其反射率，其比值为对比率，对比率等于0.98时，即为全部遮盖，根据漆膜厚度就可求得遮盖力。适用于白色及浅色漆。
CAS号：
性质：色漆、油墨等经均匀涂覆后，其涂膜遮盖被涂表面底色的能力。遮盖力是颜料对光线产生散射和吸收的结果。涂料遮盖力是指把色漆均匀涂布在物体表面上，使其底色不再呈现的最小用漆量。用g/m2表示。颜料遮盖率是指颜料和调墨油研磨成色浆，均匀地涂刷于黑白格底材上，使黑白格恰好被遮盖的最小用颜料量。颜料遮盖力的强弱主要决定于下列性能：(1)折射率，折射率愈大，遮盖力愈强；(2)吸收光线能力，吸收光线能力愈大，遮盖力愈强；(3)结晶度，晶形的遮盖力较强，无定形的遮盖力较弱；(4)分散度，分散度愈大，遮盖力愈强。同样重量的涂料产品，在相同的施工条件下，遮盖力高的产品可比遮盖力低的产品能涂装更多的面积。为了克服目测黑白格板遮盖力的不准确性，用反射率仪对遮盖力进行测定，把被测试样以不同厚度涂布于透明聚酯膜上，干燥后置于黑、白玻璃板上，分别测定其反射率，其比值为对比率，对比率等于0.98时，即为全部遮盖，根据漆膜厚度就可求得遮盖力。适用于白色及浅色漆。