1) cold hardening
冷作硬化，冷加工硬化
2) work hardening
加工硬化，冷作硬化
3) cold hardening
冷加工硬化
4) cold-work hardening
冷作硬化
1.
The cable and the tension bar which belong to the basic frame member of the prestressed long-span steel structure system are high strength steel members which had been subject to cold-work hardening and hot rolling and modified treatment separately.
索与拉杆分别经过冷作硬化处理和调质热处理后,构件强度大幅度提高,而延性性能大幅降低。
2.
The cold-work hardening of Q235 material is investigated through tests as the result of pre-torsion cold-work hardening research done before.
为此 ,利用前期扭转冷作硬化的研究成果 ,对工程中普遍使用的Q2 35钢筋母材加肋冷作硬化问题进行了试验研究 ,得出了在不改变Q2 35钢筋母材情况下 ,只要在工序中充分考虑预扭转冷作硬化的影响 ,就可以使冷轧带肋钢筋达到更高的等级 ,工程意义显著 。
3.
Therefore,making use of the research result of pre-torsion cold-work hardening,the Q235 reinforcing steels which are widely used in the construction were tested,aiming at the cold-work hardening problem.
为此,利用前期扭转冷作硬化的研究成果,对工程中普遍使用的Q235钢筋母材冷作硬化问题进行了实验研究,得出充分考虑扭转冷作硬化的影响,可以使建筑用钢筋达到更高的等级;因此设计了高效扭转装置,使建筑用钢筋快速达到预扭转强化的效果。
5) cold hardnening working method
冷作硬化加工方式
6) Cold Work Hardening Plate
冷作硬化板
1.
Study on the Rolling Process of 2Cr13 Cold Work Hardening Plate;
2Cr13冷作硬化板轧制工艺研究
补充资料：加工硬化
| 加工硬化 work hardening 金属材料在再结晶温度以下塑性变形时强度和硬度升高，而塑性和韧性降低的现象。又称冷作硬化。产生原因是，金属在塑性变形时，晶粒发生滑移，出现位错的缠结，使晶粒拉长、破碎和纤维化，金属内部产生了残余应力等。加工硬化的程度通常用加工后与加工前表面层显微硬度的比值和硬化层深度来表示。 加工硬化给金属件的进一步加工带来困难。如在冷轧钢板的过程中会愈轧愈硬以致轧不动，因而需在加工过程中安排中间退火，通过加热消除其加工硬化。又如在切削加工中使工件表层脆而硬，从而加速刀具磨损、增大切削力等。但有利的一面是，它可提高金属的强度、硬度和耐磨性，特别是对于那些不能以热处理方法提高强度的纯金属和某些合金尤为重要。如冷拉高强度钢丝和冷卷弹簧等，就是利用冷加工变形来提高其强度和弹性极限。又如坦克和拖拉机的履带、破碎机的颚板以及铁路的道岔等也是利用加工硬化来提高其硬度和耐磨性的。 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。