1) tungsten carbide surfacing electrode
碳化钨堆焊焊条
2) Deposit welding rod
堆焊焊条
1.
Research on the wear-resisting and heat-resisting deposit welding rode;
耐磨耐热堆焊焊条的制备研究
2.
The wear-resisting and heat-resisting deposit welding rod with Ni-Co-Cr-B-C as the basic alloy system was prepared by mechanical ball milling mixture, sintering after extrusion shaping method.
选择Ni-Co-Cr-B-C为基本合金体系,经过机械球磨混合、挤压成形、真空烧结方法制备了耐磨耐热堆焊焊条,采用钨极氩弧焊在高温铸造合金基材上堆焊耐磨耐热堆焊层,对堆焊层的组成、结构进行了分析,XRD分析和热力学计算表明焊层组成为Co、Ni为主的面心立方合金、M23(C,B)6或M23C6,还有少量的C7M3和M3B2。
3) Hardfacing electrode
堆焊焊条
1.
Welding process of high temperature and non-slag hardfacing electrode;
高温无渣耐磨堆焊焊条的焊接工艺
2.
A hardfacing electrode containing boron and various alloy elements has been developed.
研制出一种含硼等多种合金元素的耐高温磨损堆焊焊条。
4) surfacing electrode
堆焊焊条
1.
Development of wear resisting surfacing electrode with high efficiency,high hardness and low cost;
高效高硬度低成本耐磨堆焊焊条的研制
2.
Research on cavitation-resistant surfacing electrode;
Cr-Mn抗气蚀堆焊焊条
3.
Research of alloy chute surfacing electrode;
合金溜槽堆焊焊条的研制
6) interspersed carbide
敷焊用碳化钨粉
补充资料：碳化钨
化学式WC。为黑色六方晶体，有金属光泽，硬度与金刚石相近，为电、热的良好导体。熔点2870℃, 沸点6000℃，相对密度 15.63(18℃)。碳化钨不溶于水、盐酸和硫酸，易溶于硝酸－氢氟酸的混合酸中。纯的碳化钨易碎，若掺入少量钛、钴等金属，就能减少脆性。用作钢材切割工具的碳化钨，常加入碳化钛、碳化钽或它们的混合物，以提高抗爆能力。碳化钨的化学性质稳定。
在碳化钨中，碳原子嵌入钨金属晶格的间隙，并不破坏原有金属的晶格，形成填隙固溶体，因此也称填隙（或插入）化合物（见图）。碳化钨可由钨和碳的混合物高温加热制得，氢气或烃类的存在能加速反应的进行。若用钨的含氧化合物进行制备，产品最终必须在1500℃进行真空处理, 以除去碳氧化合物。碳化钨适宜在高温下进行机械加工，可制作切削工具、窑炉的结构材料、喷气发动机、燃气轮机、喷嘴等。
钨与碳的另一个化合物为碳化二钨，化学式为 W2C，熔点为2860℃，沸点6000℃,相对密度17.15。其性质、制法、用途同碳化钨。
在碳化钨中，碳原子嵌入钨金属晶格的间隙，并不破坏原有金属的晶格，形成填隙固溶体，因此也称填隙（或插入）化合物（见图）。碳化钨可由钨和碳的混合物高温加热制得，氢气或烃类的存在能加速反应的进行。若用钨的含氧化合物进行制备，产品最终必须在1500℃进行真空处理, 以除去碳氧化合物。碳化钨适宜在高温下进行机械加工，可制作切削工具、窑炉的结构材料、喷气发动机、燃气轮机、喷嘴等。
钨与碳的另一个化合物为碳化二钨，化学式为 W2C，熔点为2860℃，沸点6000℃,相对密度17.15。其性质、制法、用途同碳化钨。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。