1) alumetized steel electrode
渗铝钢焊条
2) aluminized steel tube welding
渗铝钢管焊接
3) aluminizing carbon steel
渗铝碳钢
1.
The influence on aluminizing carbon steel of temperature,partial pressure of CO2,mineralization and pH value was studied through zero-G test.
在高压釜中对N80钢和渗铝碳钢材料进行了CO2腐蚀试验。
4) Aluminized steel
渗铝钢
1.
Application of aluminized steel in sulphuric acid plant;
渗铝钢在硫酸装置中的应用
2.
Spinodal Decomposition Structures in Diffusion Layer of Aluminized Steel and Its Formation Mechanism;
渗铝钢中的调幅分解及其形成原因
5) aluminized mild steel
碳钢渗铝
1.
The results showed that the susceptibility to H2S corrosion cracking of the weld seam is higher than that of the relevant matrix; the SCC susceptibility of Aluminized Mild Steel is lower than that of steels of 20# and 16MnR; The application of aluminized mild steel to heat exchanger was suggested.
用双U形恒应变实验方法,研究了20#碳钢、16MnR、碳钢渗铝基材及焊接材料浸泡在不同硫化物浓度的油品介质中的开裂敏感性。
6) aluminizing steel
渗铝钢
1.
The effect of internal oxidation in the diffusion layer on cyclic oxidation resistance of aluminizing steel was investigated.
通过循环氧化试验和SEM观察,研究了内氧化对扩散型热浸渗铝钢循环氧化性能的影响。
2.
resistant welded joint of 20 aluminizing steel pipes welded with common stainless steel E309MoL electrode can be obtained when the correct groove processing method and proper welding technique were adopted.
通过焊接接头的力学性能试验、金相组织分析以及工程实践证明,采用普通不锈钢E309MoL焊条焊接 20渗铝钢管道,只要采用正确的坡口加工方法和合理的焊接工艺,即可获得具有抗高温氧化和耐H2S等介质腐蚀 的焊接接头。
补充资料：渗铝钢
分子式：
CAS号：
性质：利用热浸渗铝方法改善耐蚀性和耐热性的钢。具体做法是将钢制件浸没于熔融铝浴中完成的，方法简单，易于连续作业。但因铝的熔点高达660℃，待渗铝的钢件需要进行前处理和活化处理，并要防止铝的氧化。钢板、钢带和线材均可进行表面渗铝，渗铝层的厚度可达0.05mm。一般渗铝钢的耐热温度可达700℃，其热反射性能也很好，可将75%左右的辐射热反射掉。渗铝钢可用于马弗炉、局部加热装置、采暖炉等。
CAS号：
性质：利用热浸渗铝方法改善耐蚀性和耐热性的钢。具体做法是将钢制件浸没于熔融铝浴中完成的，方法简单，易于连续作业。但因铝的熔点高达660℃，待渗铝的钢件需要进行前处理和活化处理，并要防止铝的氧化。钢板、钢带和线材均可进行表面渗铝，渗铝层的厚度可达0.05mm。一般渗铝钢的耐热温度可达700℃，其热反射性能也很好，可将75%左右的辐射热反射掉。渗铝钢可用于马弗炉、局部加热装置、采暖炉等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。